Abstract:Al-Cu alloy has broad application prospects in the field of aerospace due to its excellent performance. In this paper, deposits with different Cu contents were prepared by the wire arc additive manufacturing (WAAM) process, and the effects of Cu content on the microstructure and mechanical properties were investigated. The microstructure of Al-Cu alloy was investigated by metallography, scanning electron microscope (SEM), energy-dispersive spectrometer (EDS), and transmission electron microscope (TEM). The results show that both the number and size of the precipitated θ phases (Al2Cu) in the as-deposited material increase with the increase of Cu content. After the T4 treatment, the solid solution amount of Cu in the matrix showed a trend of first increasing and then remaining stable. When the content of Cu was greater than 5.65%, as the Cu content increased, the number and size of the remaining θ phases both increased. In the peak ageing state, the amount of precipitated θ’ phase showed a trend of increasing and then remaining stable. After the T6 treatment, the mechanical properties showed a trend of first increasing and then decreasing with the increase of the content of Cu. When the Cu content was 5.65%, the deposit achieved the best mechanical properties, and the anisotropy of the mechanical properties disappeared. The tensile strength, yield strength, and elongation reached 538 MPa, 478 MPa, and 10.5%, respectively. When the content of Cu was greater than 5.65%, the anisotropy of mechanical properties was obvious, and the fracture mode of the vertical specimen changed from ductile fracture to brittle fracture.

Effect of Cu Content on Wear Resistance and Mechanical Behavior of Ti–Cu Binary Alloys

The Effect of A Small Amount of Tungsten on the Microstructure of Mechanically Alloyed Ag37cu63

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

The Effect of Copper Content on the Mechanical and Tribological Properties of Hypo-, Hyper- and Eutectoid Ti-Cu Alloys

Effect of Cu Content on the Precipitation Behaviors, Mechanical and Corrosion Properties of As-Cast Ti-Cu Alloys

Theoretical Investigation of Cu Influence on the Stability Characteristics of T-phase in Crossover Alloys

Influence of Cu content on mechanical and tribological properties of Al–7Si–Cu alloy

The effect of Cu content on corrosion, wear and tribocorrosion resistance of Ti-Mo-Cu alloy for load-bearing bone implants

Effect of Cu content on high-temperature tribological properties and oxidation behavior of Al-Ti-V-Cu-N coatings deposited by HIPIMS

Effect of Ti content on microstructure and mechanical properties of CuCoFeNi high-entropy alloys

Influence of Cu Content Variation on the Tribological Properties of Ni60CuMo with Sandwich-Structured Composite Coatings by Laser Cladding

Effects of Cu on the high-entropy alloys of Cu x CoCrFeNi: Experiment and molecular dynamics simulations

Impact of Cu Content on Microstructural Evolution and Mechanical Behavior of CoCrMo0.5TiVCux High-Entropy Alloys

Effect of Cu content on microstructure and properties of Ti-6Al-4V alloy fabricated by double-wire arc additive manufacturing

Effect of Cu doping on the microstructure and mechanical properties of AlTiVN-Cu nanocomposite coatings

Microstructure and mechanical properties of Cu-12 Al-6 Ni with Ti addition prepared by powder metallurgy

Structural, Electrical and Corrosion Properties of Bulk Ti–Cu Alloys Produced by Mechanical Alloying and Powder Metallurgy

Effects of Ni content on microstructure and wear behavior of Al–13Si–3Cu–1Mg-xNi-0.6Fe-0.6Mn alloys

The Effect of Cu Content on the Microstructure and Properties of the Wire Arc Additive Manufacturing Al-Cu Alloy

Effect of Ti–Cu alloy's composition on microstructure and performance of carbon fiber reinforced TiC-based composites prepared by alloyed reactive melt infiltration

Effect of Cu-doping on tribological properties of laser-cladded FeCoCrNiCu x high-entropy alloy coatings