Abstract:Carbon nanotube (CNT) aerogels with varying and controllable density were fabricated from low-cost raw materials via simple steps based on sol–gel technique. CNT raw powders were dispersed in water with sodium dodecyl benzene sulfonate as surfactant under ultrasonic wave, which then coagulated into gel at room temperature. The gels were thoroughly washed by using hot (90 °C) polyvinyl alcohol (PVA) aqueous solution (mass ratio = 1 %) and then centrifuged. Finally, after solvent exchange, the gels were converted into aerogels by using supercritical CO2 fluid drying process. Free-standing and monolithic CNT aerogels with varying and controllable density (~0.06–0.35 g/cm3), elastic modulus (~0.17–0.87 MPa), electric conductivity (~0.56–4.55 S/m), specific surface area (SSA, ~100 m2/g), and average pore diameter (10–20 nm) were obtained. The density of CNT aerogels was correlated with the relative intensity ratio of the D band to the G band (ID/IG) in Raman spectrum as well, which indicated the degree of order. The residual PVA molecules intertwined CNTs, which pulled the SSA down and increased the degree of disorder of CNT aerogel in some extent. The low-cost CNT aerogels with varying and controllable density are meaningful in providing a competitive candidate for potential target materials in inertial confinement fusion experiments and laser-driven quasi-isentropic compression experiments.Graphical AbstractFree-standing and monolithic carbon nanotube (CNT) aerogels with varying and controllable density were fabricated from low-cost raw materials via simple steps based on sol–gel technique, which mainly includes dispersion, centrifugation, and drying. CNT aerogels exhibited varying and controllable density (~0.06–0.35 g/cm3), elastic modulus (~0.17–0.87 MPa), electric conductivity (~0.56 to 4.55 S/m), specific surface area (SSA, ~100 m2/g), average pore diameter (10–20 nm), and cross-linked micrograph. In addition, the Raman spectrum of CNT aerogels was given, and the correlations between density and ID/IG were discussed. The low-cost CNT aerogels with varying and controllable density are meaningful in providing a competitive candidate for potential target materials in inertial confinement fusion experiments and laser-driven quasi-isentropic compression experiments.

Self-Expansion Construction of Ultralight Carbon Nanotube Aerogels with a 3D and Hierarchical Cellular Structure.

Ultralight, Elastic, Magnetic and Superhydrophobic Cellulose Nanofibril Based Aerogel with Layer-Support Structure Designed for Both Excellent Oil-Water Separation and Efficient PM2.5 Removal

Ultralight Multiwalled Carbon Nanotube Aerogel.

Preparation of Stable Carbon Nanotube Aerogels with High Electrical Conductivity and Porosity

Facile Preparation of Carbon Nanotube Aerogels with Controlled Hierarchical Microstructures and Versatile Performance

Self-assembly of 3D Carbon Nanotube Sponges: A Simple and Controllable Way to Build Macroscopic and Ultralight Porous Architectures.

Preparation of micro-convex rough interface carbon aerogels with cellulose-lithium bromide (LiBr) molten salt hydrate gelled system and application of oil-water separation

Extrusion 3D Printing of Carbon Nanotube-Assembled Carbon Aerogel Nanocomposites with High Electrical Conductivity

Ultralight Multifunctional Carbon-Based Aerogels by Combining Graphene Oxide and Bacterial Cellulose

A Direct Foaming Approach for Carbon Nanotube Aerogels with Ultra-Low Thermal Conductivity and High Mechanical Stability.

Robust Carbonaceous Nanofiber Aerogels from All Biomass Precursors

Directly Mass-Production Growing Method Of Cnt Aerogel With Superb Liquid-Absorption Capability

Low-cost carbon nanotube aerogels with varying and controllable density

Ambient-drying to construct unidirectional cellulose nanofibers/ carbon nanotubes aerogel with ultra-lightweight, robust, and superior microwave absorption performance

Sonication-Free Dispersion of Single-Walled Carbon Nanotubes for High-Sorption-Capacity Aerogel Fabrication

Wood‐Derived Ultrathin Carbon Nanofiber Aerogels

Chemical Foaming Coupled Self-Etching: A Multiscale Processing Strategy for Ultrahigh-Surface-Area Carbon Aerogels.

Devisable pore structures and tunable thermal management properties of aerogels composed of carbon nanotubes and cellulose nanofibers with various aspect ratios

Assembly of partially unzipped multiwalled carbon nanotubes into ultralight, highly efficient and multifunctional electromagnetic wave absorbing aerogel

Electrically Conductive Aerogels Composed of Cellulose and Carbon Nanotubes

Carbon Nanotube Sponges, Aerogels, and Hierarchical Composites: Synthesis, Properties, and Energy Applications