Abstract:Nano-scaled pure and iron doping Titanium Dioxide prepared by TiCl4 hydrolysis were obtained. Two methods, step precipitation and co-precipitation, were applied in preparing the iron doping samples. The crystallization and decomposition processes were extensively investigated by methods of X-ray diffraction and TEM. The grain sizes under series of calcinating temperatures were computed according to Voigt function analysis. The results of TEM images also justified the computed grain size. The results showed that Titanium Dioxide prepared by TiCl4 hydrolysis is amorphous, and that no obvious: crystallization temperature or exothermic peaks were observed, contrary to the some previous reports. The computation applying the nuclei growth equation showed that the crystal grain growth of the pure and co-precipitation samples can be divided into 2 steps. The growth activation energy of the former step is 10.7kJ . mol(-1) and 8.6kJ . mol(-1), respectively and that of the latter step is 111.6kJ . mol(-1). As to the step precipitation samples, there showed no obvious difference in crystal growth activation energies for the 2 steps, and for the transformation of anantase to rutile was almost completed before 600 degrees C. There was evidence that the iron doping accelerated the transformation of rutile to anatase and this is especially obvious in step precipitation samples.

Room-Temperature Ferromagnetism in TiO2 Nanocrystals Synthesized by the Controlled Hydrolysis Procedure.

Ferromagnetism at Room Temperature in Cr-Doped Anodic Titanium Dioxide Nanotubes

Strong Room-Temperature Ferromagnetism in Co2+-Doped TiO2 made from Colloidal Nanocrystals

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

Room-Temperature Ferromagnetism in Ti1-Xvxo2 Nanocrystals Synthesized from an Organic-Free and Water-Soluble Precursor

Room-temperature Ferromagnetism in Fe-doped PbTiO3 Nanocrystals

Room-Temperature Ferromagnetism in Fe-Doped Na0.5bi0.5tio3 Crystals

Structure and magnetic properties of Co-doped TiO2 nanotubes by aqueous solution method

Effects of Preparation Parameters on Room Temperature Formation of Vanadium-Doped Tio2 Nanocrystalline Powder

Magnetic Properties Of V-Doped Tio2 Nanocrystalline Film Synthesized By Liquid Phase Deposition Technique

Magnetic Characteristics of Carbon-Doped Nanocrystalline TiO$_{2}$

Room-Temperature Ferromagnetism in (mn, N)-Codoped Tio2 Films Grown by Plasma Assisted Molecular Beam Epitaxy

The Magnetic Property of Carbon-Doped Tio2

Improved Room-Temperature Ferromagnetism in Self-Assembled Disk-Like Superstructures of Fe-Doped Pbtio3 Nanocrystals

Room-Temperature Ferromagnetism in Co-Doped SrTiO3 Nanofibres

Ferromagnetic Property of Co and Ni Doped Tio2 Nanoparticles

Hydrogenation Induced Transformation of Paramagnetism to Room-Temperature Ferromagnetism in Co-Doped TiO2 Ceramics

Ferromagnetism in Nitrogen-Doped Nanoparticles

Room-temperature ferromagnetism of Co-doped Na0.5Bi0.5TiO3: Diluted magnetic ferroelectrics

Room-temperature ferromagnetism in co-doped SrTiO 3 nanofibres

Room-temperature ferromagnetism in bulk Co_xTi_(1-x)O_(2-δ) induced by the phase transformation in the hydrogenation sintering process