[Influence of Coca-Cola on Early Erosion and Surface Microhardness of Human Enamel: an in Situ Study].

M Yuan,Q Zhang,X J Gao

DOI: https://doi.org/10.3760/cma.j.issn.1002-0098.2016.06.008

2016-01-01

Abstract:OBJECTIVE:Assessed the effect of single dose attack of Coca-Cola on early erosion and surface microhardness of permanent human enamel, in order to provide diet instructions on minimum amount and frequency of carbonated beverage consumption.METHODS:Eighty enamel slabs were prepared out of 10 extracted human mandibular third molars, and distributed into 8 groups with randomized block design(n=10). Ten generally healthy volunteers with normal saliva secretion wore acrylic palatal appliances containing 2 enamel slabs, with formation of a salivary pellicle 2 h ahead. The volunteers were instructed to drink 100 ml fresh Coca-Cola within 20 s. And then the alterations of the enamel slabs were measured using a Vicker's microhardness tester at 1, 2, 4, 6, 8, 10, 20 and 30 min after the consumption of Coca-Cola. For each volunteer, the experiment was carried out in four days, 2 samples were examined each time. Data were analyzed using Kruskal-Wallis and Wilcoxon tests(α =0.05).RESULTS:Significant decreases in surface microhardness(SMH)were observed in each time point(P<0.01). The percentages of surface microhardness changes on each exposure time were(12.2±3.9)%,(16.8±5.5)%,(16.7±5.6)%,(16.2±6.2)%,(16.6±9.0)%,(15.6±3.7)%,(13.8±4.8)% and(11.4±3.2)%, respectively. Significant differences were observed between G1 min and G2-8 min(P=0.029), G2-8 min and G30 min(P=0.008).CONCLUSIONS:Single intake of 100 ml Coca-Cola could lead to significant decrease of enamel microhardness and initiate erosion of enamel surface. Enamel surface microhardness decreased to the lowest points at 2-8 min, and began to recover after 10 min. The enamel surface microhardness could not fully recovered to the baseline level in 30 min if no intervention was performed.