Abstract:Pyrolysis of biomass with and without a catalyst was investigated using thermogravimetric analysis coupled with Pyrolysis-Gas Chromatography/Mass Spectrometry. The effect of two completely different catalysts (a basic catalyst:CaO, and an acidic catalyst:HZSM-5) on pyrolysis characteristics and the composition of pyrolysis vapors, as well as aromatic selectivity, were studied. A characteristic analysis of catalysts (using XRD, BET, FTIR, NH3-TPD and SEM), the effect of catalytic temperature, the CaO to HZSM-5 ratio and the biomass to catalyst ratio on the distribution of products were also investigated and analyzed. Coke formation and deposition mechanisms and the relationship between the formation and characteristics of the coke and the deactivation of the catalyst were also demonstrated. The results demonstrate that the pyrolysis characteristics of the biomass were changed by the addition of CaO (bond breaking) and HZSM-5 (deoxygenation) catalysts, causing the solid residue rate to increase significantly, the maximum weight loss rate to decrease and the biomass conversion rate to increase. The order of the activity of the catalysts is HZSM-5 > CaO/HZSM-5 > CaO; at the same time, characteristic parameters such as activation energy, activation enthalpy, activation entropy and the steric parameter increased significantly at the expense of the reaction ratio. Moreover, CaO mixed with HZSM-5 catalyst can improve the gas content and aromatic hydrocarbon content significantly. However, the content of bio-oil decreased slightly, and the maximum aromatic content was 72 wt% of peak area of that for pure HZSM-5 catalyst (69 wt% of peak area) at a pyrolysis temperature of 450 degrees C and a catalytic temperature of 550 degrees C. The ratio of CaO to HZSM-5 was 1:2, and the biomass to catalyst ratio was 1:2. In addition, the selectivities with toluene and xylene were 27% and 35%, respectively. This paper describes a process for the high-value utilization of biomass as a sustainable resource for the production of hydrocarbons, especially for the preparation of the high-quality chemical p-xylene.

Enhancing the Production of Light Olefins and Aromatics from Catalytic Fast Pyrolysis of Cellulose in a Dual-Catalyst Fixed Bed Reactor

Catalytic Fast Pyrolysis of Cellulose in a Microreactor System Using Hierarchical Zsm-5 Zeolites Treated with Various Alkalis

Preparation of aromatics from fast catalytic pyrolysis of cellulose over alkali-treated HZSM-5

Catalytic Fast Pyrolysis of Rice Straw to Aromatic Compounds over Hierarchical HZSM-5 Produced by Alkali Treatment and Metal-Modification

[Influence of ZSM-5(38)/Al-MCM-41 Composite Molecular Sieve Catalysts on Pyrolysis of Cellulose].

Enhancement in the Aromatic Yield from the Catalytic Fast Pyrolysis of Rice Straw over Hexadecyl Trimethyl Ammonium Bromide Modified Hierarchical HZSM-5

Enhancing High Selectivity Production of Light Aromatics from In-Situ Catalytic Upgrading of Cellulose Pyrolysis Vapors by Regulating Hierarchical Core-Shell ZSM-5@MCM-41

Study on the Pyrolysis of Cellulose for Bio-Oil with Mesoporous Molecular Sieve Catalysts.

Catalytic Pyrolysis of Hemicellulose for the Production of Light Olefins and Aromatics over Fe Modified ZSM-5 Catalysts

Catalytic Fast Pyrolysis of Cellulose over Different Metal-Modified ZSM-5 Zeolites for Light Olefins

Improving Hydrocarbon Yield from Catalytic Fast Co-Pyrolysis of Hemicellulose and Plastic in the Dual-Catalyst Bed of CaO and HZSM-5.

Promotion of Monocyclic Aromatics by Catalytic Fast Pyrolysis of Biomass with Modified HZSM-5

On-line catalytic cracking of vapors from cellulose fast pyrolysis

Enhancing the aromatic hydrocarbon yield from the catalytic copyrolysis of xylan and LDPE with a dual-catalytic-stage combined CaO/HZSM-5 catalyst

Improving catalytic production of aromatic hydrocarbons with a mesoporous ZSM-5 modified with nanocellulose as a green template

Improving the Aromatic Production in Catalytic Fast Pyrolysis of Cellulose by Co-Feeding Low-Density Polyethylene

Aromatics production with metal oxides and ZSM-5 as catalysts in catalytic pyrolysis of wood sawdust

Improving Aromatic Hydrocarbon Content from Catalytic Pyrolysis Upgrading of Biomass on a CaO/HZSM-5 Dual-Catalyst

Catalytic Upgrading of Fast Pyrolysis Products with Fe-, Zr-, and Co-Modified Zeolites Based on Pyrolyzer–GC/MS Analysis

Porosity roles of micro-mesostructured ZSM-5 in catalytic fast pyrolysis of cellulolytic enzyme lignin for aromatics

Catalytic co-pyrolysis of seaweeds and cellulose using mixed ZSM-5 and MCM-41 for enhanced crude bio-oil production