Abstract:A novel micro/nanoscale rough structured superhydrophilic hybrid-coated mesh that shows underwater superoleophobic behavior is fabricated by spray casting or dipping nanoparticle–polymer suspensions on stainless steel mesh substrates. Water droplets can spread over the mesh completely; meanwhile, oil droplets can roll off the mesh at low tilt angles without any penetration. Besides overcoming the oil-fouling problem of many superhydrophilic coatings, this superhydrophilic and underwater superoleophobic mesh can be used to separate oil and water. The simple method used here to prepare the organic–inorganic hybrid coatings successfully produced controllable micro-nano binary roughness and also achieved a rough topography of micro-nano binary structure by controlling the content of inorganic particles. The mechanism of oil–water separation by the superhydrophilic and superoleophobic membrane is rationalized by considering capillary mechanics. Tetraethyl orathosilicate (TEOS) as a base was used to prepare the nano-SiO2 solution as a nano-dopant through a sol-gel process, while polyvinyl alcohol (PVA) was used as the film binder and glutaraldehyde as the cross-linking agent; the mixture was dip-coated on the surface of 300-mesh stainless steel mesh to form superhydrophilic and underwater superoleophobic film. Properties of nano-SiO2 represented by infrared spectroscopy and surface topography of the film observed under scanning electron microscope (SEM) indicated that the film surface had a coarse micro–nano binary structure; the effect of nano-SiO2 doping amount on the film’s surface topography and the effect of such surface topography on hydrophilicity of the film were studied; contact angle of water on such surface was tested as 0° by the surface contact angle tester and spread quickly; the underwater contact angle to oil was 158°, showing superhydrophilic and underwater superoleophobic properties. The effect of the dosing amount of cross-linking agent to the waterproof swelling property and the permeate flux of the film were studied; the oil–water separation effect of the film to oil–water suspension and oil–water emulsion was studied too, and in both cases the separation efficiency reached 99%, which finally reduced the oil content to be lower than 50 mg/L. The effect of filtration times to permeate flux was studied, and it was found that the more hydrophilic the film was, the stronger the stain resistance would be, and the permeate flux would gradually decrease along with the increase of filtration times.

Femtosecond Laser Induced Robust Periodic Nanoripple Structured Mesh For Highly Efficient Oil-Water Separation

Laser Manufacturing of Superwetting Oil–Water Separation Materials: A Review

Ni-Al Layered Double Hydroxides (ldhs) Coated Superhydrophobic Mesh with Flower-Like Hierarchical Structure for Oil/water Separation

Spatial Light Modulated Femtosecond Laser Ablated Durable Superhydrophobic Copper Mesh for Oil-Water Separation and Self-Cleaning

Laser-induced Stainless Steel Mesh for High Effective Water/oil Separation

Fabrication of a Novel Superhydrophobic and Superoleophilic Surface by One-Step Electrodeposition Method for Continuous Oil/water Separation

Durable Superhydrophobic Engineered Mesh with Self-Healing and Anti-Corrosive Capabilities for Efficient Oil/water Separation

Ultrafast nano-structuring of superwetting Ti foam with robust antifouling and stability towards efficient oil-in-water emulsion separation.

Preparation of Superhydrophilic and Underwater Superoleophobic Nanofiber-Based Meshes from Waste Glass for Multifunctional Oil/Water Separation.

Nanoscale SiO2-coated superhydrophobic meshes via electro-spray deposition for oil-water separation

Nanoscale SiO<sub>2</sub>-coated superhydrophobic meshes via electro-spray deposition for oil-water separation

Buoyant and Durable Oil/water Separation Mesh for Continuous and Efficient Collection of Both Oil Slick and Underwater Oil Leakage

Preparation of Superhydrophilic and Underwater Superoleophobic Nanofiber‐Based Meshes from Waste Glass for Multifunctional Oil/Water Separation

A Pair of MnO2 Nanocrystal Coatings with Inverse Wettability on Metal Meshes for Efficient Oil/water Separation

A durable Ni3S2 coated mesh with reversible transition between superhydrophobicity and underwater superoleophobicity for efficient oil-water separation

Robust Photopolymerized Superoleophobic/Superhydrophilic Mesh for Oil-Water Separation

Laser Composite Fabrication of Super-Wetting Membrane with Micro Square Hole-Nanowire Structure for Oil-Water Separation

Environmentally Benign Development of Superhydrophilic and Underwater Superoleophobic Mesh for Effective Oil/water Separation

Micro/Nanoscale Structured Superhydrophilic and Underwater Superoleophobic Hybrid-Coated Mesh for High-Efficiency Oil/Water Separation

Facile Fabrication of the Durable Micro/nano-Superhydrophilic/superoleophobic Surface Through One-Step Spraying for Efficient Oil–water Separation

Surface Modification to Fabricate Dual Superlyophobic Mesh for Efficient Oil/water Separation