Abstract:Abstract Graphene oxide (GO), reduced graphene oxide (rGO) and carbon nanotubes (CNTs) have their own advantages in electrical, optical, thermal and mechanical properties. An effective combination of these materials is ideal for preparing transparent conductive films to replace the traditional indium tin oxide films. At present, the preparation conditions of rGO are usually harsh and some of them have toxic effects. In this paper, an SnCl 2 /ethanol solution was selected as the reductant because it requires mild reaction conditions and no harmful products are produced. The whole process of rGO preparation was convenient, fast and environmentally friendly. Then, SEM, XPS, Raman, and XRD were used to verify the high reduction efficiency. CNTs were introduced to improve the film conductive property. The transmittance and sheet resistance were the criteria used to choose the reduction time and the content ratios of GO/CNT. Thanks to the post-treatment of nitric acid, not only the by-product (SnO 2 ) and dispersant in the film are removed, but also the doping effect occurs, which are all conducive to reducing the sheet resistances of films. Ultimately, by combining rGO, GO and CNTs, transparent conductive films with a bilayer and three-dimensional structure were prepared, and they exhibited high transmittance and low sheet resistance (58.8 Ω/sq. at 83.45 T%, 47.5 Ω/sq. at 79.07 T%), with corresponding $${{\sigma_{dc} } \mathord{\left/ {\vphantom {{\sigma_{dc} } {\sigma_{opt} }}} \right. \kern-\nulldelimiterspace} {\sigma_{opt} }}$$ σ dc / σ opt values of 33.8 and 31.8, respectively. In addition, GO and rGO can modify the surface and reduce the film surface roughness. The transparent conductive films are expected to be used in photoelectric devices.

A Facile Reduction Method for Roll-To-Roll Production of High Performance Graphene-Based Transparent Conductive Films

A Fast Room-Temperature Strategy for Direct Reduction of Graphene Oxide Films Towards Flexible Transparent Conductive Films

Reduced graphene oxide nanoribbon networks: a novel approach towards scalable fabrication of transparent conductive films.

High-efficiency and room-temperature reduction of graphene oxide: a facile green approach towards flexible graphene films.

Rod-coating: towards large-area fabrication of uniform reduced graphene oxide films for flexible touch screens.

A Green and Mild Approach of Synthesis of Highly-Conductive Graphene Film by Zn Reduction of Exfoliated Graphite Oxide

A New Reducing Agent to Prepare Single-Layer, High-Quality Reduced Graphene Oxide for Device Applications

Preparation of Reduced Graphene Oxide by Infrared Irradiation Induced Photothermal Reduction

Enhanced Transparent Conductive Properties of Graphene/Carbon Nano-Composite Films

Reduced Graphene Oxide Films with Ultrahigh Conductivity As Li-Ion Battery Current Collectors

Low-cost Preparation of a Conductive and Catalytic Graphene Film from Chemical Reduction with AlI3

A Facile and Cost-Effective Approach to the Reduction of Exfoliated Graphite Oxide Using Sodium Hypophosphite under Acidic Conditions

One-step Growth of Reduced Graphene Oxide on Arbitrary Substrates

Reduction of graphene oxide to highly conductive graphene by Lawesson's reagent and its electrical applications

High-quality Single-Layer Graphene Via Reparative Reduction of Graphene Oxide

Low-Cost Preparation of Graphene Papers from Chemical Reduction with Fei2/Ni2+ for Conductivity and Catalytic Property

Electrochromic Properties of Ni/NiO/rGO Nanocomposite Films Prepared by a Facile Sol-Gel Technique

Bilayer and three dimensional conductive network composed by SnCl2 reduced rGO with CNTs and GO applied in transparent conductive films

Roll-to-roll Production of 30-Inch Graphene Films for Transparent Electrodes

Highly Conductive Free-Standing Reduced Graphene Oxide Thin Films for Fast Photoelectric Devices

Surface And Interface Engineering Of Graphene Oxide Films By Controllable Photoreduction