Abstract:Wafer-like porous xLiV(3)O(8)-yLi(0.3)V(2)O(5) (Li-V-O) composites are synthesized by a facile self-assembled synthesis using a glycine-assisted solution route followed by a low-temperature reaction. The crystalline compounds have a uniform shape and distribution of sizes, and the primary particles are platelike in shape with 150-500 nm in length and 80-200 nm in width. Such porous materials have many advantages such as good electrical contact among the particles and easy for electrolyte to penetrate the active materials, thus facilitating improvement in the electrochemical performance of Li-intercalation cathode. Among these Li-V-O composites, the one synthesized at 400 degrees C, which has 27.06 wt % Li(0.3)V(2)O(5), exhibits the highest initial discharge capacities of 300.5, 265.7, and 237.0 mAh g(-1) at current densities of 20 (C/15), 50 (C/6), and 120 mA g(-1) (0.4 C) between 2.0 and 4.0 V, respectively. The good electrochemical performance of the as-synthesized composite can be attributed to the porous structure, thus highly favors the solid-state diffusion kinetics and enhances the capacity of the Li-V-O electrode. The ease of synthetic preparation of this novel porous Li-V-O composite together with its good electrochemical performance shows promise application in lithium ion batteries.

Template-Free Synthesis of Highly Porous V2o5 Cuboids with Enhanced Performance for Lithium Ion Batteries

Low-cost Synthesis of Hierarchical V2O5 Microspheres As High-Performance Cathode for Lithium-Ion Batteries.

Template-free Synthesis of Hierarchical Vanadium-Glycolate Hollow Microspheres and Their Conversion to V2O5 with Improved Lithium Storage Capability.

Self-Assembled Synthesis of Hierarchical Waferlike Porous Li–V–O Composites As Cathode Materials for Lithium Ion Batteries

NaCl-template-assisted Freeze-Drying Synthesis of 3D Porous Carbon-Encapsulated V2O3 for Lithium-Ion Battery Anode

Porous Monodisperse V2O5 Microspheres As Cathode Materials for Lithium-Ion Batteries

Synthesis of V2o5 Hierarchical Structures for Long Cycle-Life Lithium-Ion Storage

Synthesis of hierarchical three-dimensional vanadium oxide microstructures as high-capacity cathode materials for lithium-ion batteries.

3D porous V2O5 architectures for high-rate lithium storage

Hierarchical Zn3V3O8/C composite microspheres assembled from unique porous hollow nanoplates with superior lithium storage capability

Internal-diffusion Controlled Synthesis of V2O5 Hollow Microspheres for Superior Lithium-Ion Full Batteries

New-phased metastable V2O3 porous urchinlike micronanostructures: Facile synthesis and application in aqueous lithium ion batteries

Porous Spinel Zn(x)Co(3-x)O(4) hollow polyhedra templated for high-rate lithium-ion batteries.

Metal-Organic Framework Fabricated V2O5 Cathode Material for High-Performance Lithium-Ion Batteries

Synthesis of Co2V2O7 Hollow Cylinders with Enhanced Lithium Storage Properties Using H2O2 As an Etching Agent

Formation of highly porous CuCo2O4 nanosheet assemblies for high-rate and long-term lithium storage

Porous V2O3/C composite electrodes derived from V-MOF with advanced performance for Zn-ion battery

Template-free Synthesis of Hollow Α-Fe2o3microcubes for Advanced Lithium-Ion Batteries

Facile synthesis of porous V 2 O 3 /C composites as lithium storage material with enhanced capacity and good rate capability

Template-free synthesis of hierarchical hollow V<sub>2</sub>O<sub>5</sub> microspheres with highly stable lithium storage capacity

Facile Preparation of V2O5 Hollow Microspheres with Mesoporous on the Shell and Their Electrochemical Properties for Lithium-Ion Batteries