Abstract:A detailed micromechanical finite element analysis methodology is presented to predict the transverse tensile (fiber perpendicular) failure behavior of a unidirectional (UD) glass fiber-reinforced plastic composite ply. In order to understand the constituent-level stress–strain and damage behavior, finite element analysis is accomplished using representative volume element (RVE) that consists of random fiber distribution as observed in the microscopic image of an actual composite ply. For modeling the fiber/matrix interface failure behavior, cohesive zone module (cohesive surface/cohesive element) of Abaqus® is used. In order to capture the epoxy matrix stiffness and strength degradation, the following two different approaches are used: (i) initially, the linear Drucker–Prager plasticity model in combination with a ductile fracture criterion is used; (ii) later, a brittle failure approach such as the quadratic normal stress criterion within the framework of eXtended finite element method is used. From the detailed micromechanical analysis of the RVE, it is observed that the initial damage in the RVE occurs in the form of fiber/matrix interface decohesion. With increasing tensile load, interface crack propagates and creates a stress concentration region in the matrix material, adjacent to the crack tip. Further load application causes both interface crack tip and matrix stress concentration to move away from the load application direction. As soon as the interface crack tip reaches approximately 60° to 70° away from the load application direction, the conjunction of the matrix damage with the interface crack leads to the RVE final failure. The predicted average stress–strain curves from the above-mentioned two different epoxy matrix failure criterions (ductile and brittle) correlate very well with the experimental results, indicating that the brittle failure behavior of a UD fiber-reinforced plastic composite ply under transverse tensile load is mainly controlled by the fiber/matrix interface properties.

Numerical Study on Rupture Process of Fiber-Reinforced Composites

Characterization of Failure Behavior in Unidirectional Fiber-Reinforced Polymer Via Off-Axis Compression on Small Block Specimens.

Study of Experimental Investigation of Tensile Compress and In-plane Shear Properties Dispersibility of Composite Laminate

Study on Fracture of Fiber-Reinforced Polymeric Composites Using Spiral Notch Torsion Test

An Experimental Study on the Fracture of a Unidirectional Carbon Fiber-Reinforced Composite under Quasistatic Torsion

Study on Longitudinal Properties of SiCf/Ti-6Al-4V Composite Including Broken Fiber

Micromechanical modeling for longitudinal tensile property of unidirectional CFRP considering dispersion of fiber properties

Study on Failure Process and Mechanical Properties of Brittle Composite Matrix with Fiber Reinforcement

A Note On The Monte-Carlo Simulation Of The Tensile Deformation And Failure Process Of Unidirectional Composites

Micromechanical Modeling of Longitudinal Tensile Behavior and Failure Mechanism of Unidirectional Carbon Fiber/aluminum Composites Involving Fiber Strength Dispersion

A Multi-Scale Stochastic Fracture Model for Characterizing the Tensile Behavior of 2D Woven Composites

Investigation on the off-axis tensile failure behaviors of 3D woven composites through a coupled numerical-experimental approach

Failure analysis and experimental study on bolted composite joints based on continuum damage mechanics

A Micromechanical Model for Longitudinal Compressive Failure in Unidirectional Fiber Reinforced Composite

Numerical investigation on the variation of compressive failure mechanisms in unidirectional carbon fiber reinforced polymer

Numerical Simulation of the Fiber Fragmentation Process in Single-Fiber Composites

Microscopic Failure Mechanisms of Fiber-Reinforced Polymer Composites under Transverse Tension and Compression

Failure analysis of unidirectional FRP with fiber clusters under transverse pure shear

Micromechanical Modeling of Damage Evolution and Mechanical Behaviors of CF/Al Composites under Transverse and Longitudinal Tensile Loadings.

Failure Analysis of Fiber-Reinforced Composites under Multiaxial Cyclic Stress

Computational micromechanical modeling of transverse tensile damage behavior in unidirectional glass fiber-reinforced plastic composite plies: Ductile versus brittle fracture mechanics approach