Novel sol-gel route for expanding the glass forming region of tin phosphate glass for secondary battery electrode applications
Ahmed Ibrahim,Kazuhiko Akiyama,Irfan Khan,Bofan Zhang,Ahmed Salah Ali,Katalin Sinkó,Janos Rohonczy,Zoltán Homonnay,Ernő Kuzmann,Marta Razum,Luka Pavić,Stjepko Krehula,Marijan Marciuš,Shiro Kubuki
DOI: https://doi.org/10.1016/j.jallcom.2024.174930
IF: 6.2
2024-05-28
Journal of Alloys and Compounds
Abstract:In this paper, tin-phosphate amorphous glass and nano-crystallized ceramic materials were synthesized by sol-gel methods and heat treated at 400 °C with the composition of x SnO 2 − (100- x )P 2 O 5 ( x SnP: ' x ' from 40 to 90 mol%). The electrical and thermal properties of tin-phosphate materials were investigated by electrical impedance spectroscopy (EIS) and thermogravimetry – differential thermal analysis – mass spectroscopy (TG–DTA–MS). Moreover, the local structure of x SnP was characterized by 119 Sn-Mössbauer and magic angle spinning (MAS) 31 P NMR spectroscopies. Homogeneous glasses were obtained for x SnP with ' x ' from 50 to 80, while Sn(HPO 4 ), SnO 2 , and Sn 3 (PO 4 ) 2 nanoparticles formed in 40SnP and 90SnP compositions, respectively. The nano-crystallized 40SnP and 90SnP samples showed large electrical conductivity ( σ ) of 2.02×10 −5 and 1.04×10 −4 S cm −1 due to the conductive crystalline phases of SnP 2 O 7 and defective SnO 2 , respectively. The lower σ of about 10 −8 S cm −1 were recorded for x SnP with ' x ' from 50 to 80 owing to the decomposition of the 3D network built by phosphate tetrahedrons. 119 Sn-Mössbauer spectra proved the growing number of Sn IV O 6 units, which do not contribute to the rise of electrical conductivity. On the other hand, larger σ values of 1.79×10 −4 and 6.4×10 −3 S cm −1 were confirmed for 40SnP and 90SnP samples after heat treatment, resulting in partial reduction of Sn IV to Sn II and growing of the 3D network structure by PO 4 3− . It is concluded that highly electrically conductive x SnP samples can be synthesized by the sol-gel method followed by slow heat treatment. In addition, the battery evaluation was performed of x SnP samples as cathode and anode in a sodium-ion battery. The highest initial capacity recorded for 90SnP nano-crystallized ceramic at 37.97 mAh g −1 under a current rate of 20 mA g −1 with capacity retention (%) of 48.15% after 100 cycles as a cathode material. The anode test showed that the 40SnP nano-crystallized ceramic has the largest initial capacity of 375 mAh g −1 and after heat treatment 50SnP glass significantly increased to 425 mAh g −1 compared with 186 mAh g −1 before heat treatment. Also, the heat treatment effect on the initial capacity of 90SnP nano-crystallized ceramic with observation largest value of 470 mAh g −1 . These results open the way to maybe applying these glass and nano-crystallized ceramic materials in all-solid-state batteries.
materials science, multidisciplinary,metallurgy & metallurgical engineering,chemistry, physical