Investigation on Mechanical and Thermal Properties of Nano-Magnesium Oxide/Poly(lactic acid) Composites by Experiment and Computational Simulation
Hong Cai,Jiayue Shang,Hongxing Wang,Yan Zhang,Yinuo Zheng,Bing Han
DOI: https://doi.org/10.1007/s11665-024-10242-x
IF: 2.3
2024-10-18
Journal of Materials Engineering and Performance
Abstract:The mechanical properties and thermal stability of poly(lactic acid) (PLA) reinforced with nano-magnesium oxide modified by maleic anhydride (mMgO) were investigated. After mixing PLA with mMgO in different proportions, the composite splines were prepared by the melting injection molding process. Results indicated that with the content of mMgO increased from 0 to 4.5wt.%, the bending strength decreased from 90 to 62 MPa, 36 MPa, and 30 MPa, respectively. The tensile strength decreased from 65 to 58 MPa, 45 MPa, and 37 MPa, respectively. Simultaneously, the breaking elongation of composites gradually decreased from 3.5 to 3.3%, 1.5%, and 2.2%. In contrast, the impact strength raised by 217.7% at 3wt.% due to the uniformly dispersed mMgO in PLA. Meanwhile, the hardness increased from 84 to 105 resulting from the high bulk modulus of MgO. Additionally, the crystallinity increased from 13.28 to 44.29%, 38.65%, and 41.18%, and the crystallization half-time reduced from 2.052 to 1.088 min, 0.975 min, and 1.046 min. This demonstrated that the addition of mMgO promoted and accelerated the crystallization of PLA. Except that, according to molecular dynamics simulation results, the movement ability of molecular chains was explained from the view of mean square displacement, radial distribution function, as well as probability density of radius of gyration. Moreover, the mechanical properties of each group of sample were illustrated based on characteristic parameters including Young's modulus (E), bulk modulus (K), shear modulus (G), the ratio of bulk modulus to shear modulus (K/G), as well as Poisson's ratio υ. The research results provided an experimental basis and theoretical guidance for the design and optimization of this kind of composites.
materials science, multidisciplinary