Abstract:The catalytic conversion of dinitrogen (N-2) into ammonia under ambient conditions represents one of the Holy Grails in sustainable chemistry. As a potential alternative to the Haber-Bosch process, the electrochemical reduction of N-2 to NH3 is attractive owing to its renewability and flexibility, as well as its sustainability for producing and storing value-added chemicals from the abundant feedstock of water and nitrogen on earth. However, owing to the kinetically complex and energetically challenging N-2 reduction reaction (NRR) process, NRR electrocatalysts with high catalytic activity and high selectivity are rare. In this contribution, as a proof-of-concept, we demonstrate that both the NH3 yield and faradaic efficiency (FE) under ambient conditions can be improved by modification of the hematite nanostructure surface. Introducing more oxygen vacancies to the hematite surface renders an improved performance in NRR, which leads to an average NH3 production rate of 0.46 mu g h(-1) cm(-2) and an NH3 FE of 6.04 % at -0.9 V vs. Ag/AgCl in 0.10 m KOH electrolyte. The durability of the electrochemical system was also investigated. A surprisingly high average NH3 production rate of 1.45 mu g h(-1) cm(-2) and a NH3 FE of 8.28 % were achieved after the first 1 h chronoamperometry test. This is among the highest FEs reported so far for non-precious-metal catalysts that use a polymer-electrolyte-membrane cell and is much higher than the FE of precious-metal catalysts (e.g., Ru/C) under comparable reaction conditions. However, the NH3 yield and the FE dropped to 0.29 mu g h(-1) cm(-2) and 2.74 %, respectively, after 16 h of chronoamperometry tests, which indicates poor durability of the system. Our results demonstrate the important role that the surface states of transition-metal oxides have in promoting electrocatalytic NRR under ambient conditions. This work may spur interest towards the rational design of electrocatalysts as well as electrochemical systems for NRR, with emphasis on the issue of stability.

ZrO2/C Nanosphere Enables High‐Efficiency Nitrogen Reduction to Ammonia at Ambient Conditions

Asymmetric Empty Orbitals in ZrO2-BCN for Enhancing Electrocatalytic Hydrogenation of Nitrogen to Ammonia

Monodisperse Cu Cluster-Loaded Defective ZrO 2 Nanofibers for Ambient N 2 Fixation to NH 3

Atomically Dispersed Zinc Active Sites Efficiently Promote the Electrochemical Conversion of N2 to NH3

Boosting Electrochemical Nitrogen Fixation by Mesoporous Rh Film with Boron and Sulfur Co-Doping

Atomically Dispersed Zinc(I) Active Sites to Accelerate Nitrogen Reduction Kinetics for Ammonia Electrosynthesis

Heterogenous Cu@ZrO2 nanofibers enable efficient electrocatalytic nitrate reduction to ammonia under ambient conditions

A New Trick on an Old Support: Zr in Situ Defects-Created Carbon Nitride for Efficient Electrochemical Nitrogen Fixation

Asymmetric empty orbitals in ZrO 2 -BCN for enhancing electrocatalytic hydrogenation of nitrogen to ammonia

Interfacial Reduction Nucleation of Noble Metal Nanodots on Redox-Active Metal–Organic Frameworks for High-Efficiency Electrocatalytic Conversion of Nitrate to Ammonia

Hierarchical Cobalt Phosphide Hollow Nanocages toward Electrocatalytic Ammonia Synthesis under Ambient Pressure and Room Temperature

Metal‐Organic‐Framework‐Derived Cobalt‐Doped Carbon Material for Electrochemical Ammonia Synthesis under Ambient Conditions

Ambient N2 Fixation to NH3 at Ambient Conditions: Using Nb2O5 Nanofiber As a High-Performance Electrocatalyst

Hetero-phase zirconia encapsulated with Au nanoparticles for boosting electrocatalytic nitrogen reduction

Highly Selective Electrochemical Reduction Of Dinitrogen To Ammonia At Ambient Temperature And Pressure Over Iron Oxide Catalysts

High-performance artificial nitrogen fixation at ambient conditions using a metal-free electrocatalyst

Co3O4 nanoparticles embedded in porous carbon nanofibers enable efficient nitrate reduction to ammonia

Ni-loaded Co-NC Catalysts for Promoting Electrocatalytic Nitrate Reduction to Ammonia

Modulating Nitrogen Adsorption Mode and Microenvironment of Active Sites for Boosting Electrochemical Nitrogen Reduction

Amorphous Sn/Crystalline SnS2 Nanosheets Via in Situ Electrochemical Reduction Methodology for Highly Efficient Ambient N2 Fixation.

High-efficiency ammonia electrosynthesis via selective reduction of nitrate on ZnCo2O4 nanosheet array