Abstract:The catalytic conversion of dinitrogen (N-2) into ammonia under ambient conditions represents one of the Holy Grails in sustainable chemistry. As a potential alternative to the Haber-Bosch process, the electrochemical reduction of N-2 to NH3 is attractive owing to its renewability and flexibility, as well as its sustainability for producing and storing value-added chemicals from the abundant feedstock of water and nitrogen on earth. However, owing to the kinetically complex and energetically challenging N-2 reduction reaction (NRR) process, NRR electrocatalysts with high catalytic activity and high selectivity are rare. In this contribution, as a proof-of-concept, we demonstrate that both the NH3 yield and faradaic efficiency (FE) under ambient conditions can be improved by modification of the hematite nanostructure surface. Introducing more oxygen vacancies to the hematite surface renders an improved performance in NRR, which leads to an average NH3 production rate of 0.46 mu g h(-1) cm(-2) and an NH3 FE of 6.04 % at -0.9 V vs. Ag/AgCl in 0.10 m KOH electrolyte. The durability of the electrochemical system was also investigated. A surprisingly high average NH3 production rate of 1.45 mu g h(-1) cm(-2) and a NH3 FE of 8.28 % were achieved after the first 1 h chronoamperometry test. This is among the highest FEs reported so far for non-precious-metal catalysts that use a polymer-electrolyte-membrane cell and is much higher than the FE of precious-metal catalysts (e.g., Ru/C) under comparable reaction conditions. However, the NH3 yield and the FE dropped to 0.29 mu g h(-1) cm(-2) and 2.74 %, respectively, after 16 h of chronoamperometry tests, which indicates poor durability of the system. Our results demonstrate the important role that the surface states of transition-metal oxides have in promoting electrocatalytic NRR under ambient conditions. This work may spur interest towards the rational design of electrocatalysts as well as electrochemical systems for NRR, with emphasis on the issue of stability.

Ambient N2 Fixation to NH3 at Ambient Conditions: Using Nb2O5 Nanofiber As a High-Performance Electrocatalyst

Efficient Electrocatalytic N2 Fixation with MXene under Ambient Conditions

Au Sub-Nanoclusters on TiO 2 toward Highly Efficient and Selective Electrocatalyst for N 2 Conversion to NH 3 at Ambient Conditions.

Highly Selective Electrochemical Reduction Of Dinitrogen To Ammonia At Ambient Temperature And Pressure Over Iron Oxide Catalysts

Nitrogen-coordinated Single Fe Sites for Efficient Electrocatalytic N2 Fixation in Neutral Media

NbO2 Electrocatalyst Toward 32% Faradaic Efficiency for N-2 Fixation

Nanoporous NiBi catalyst for efficient electrochemical N 2 fixation

An amorphous WC thin film enabled high-efficiency N<sub>2</sub> reduction electrocatalysis under ambient conditions

Porous LaFeO3 nanofiber with oxygen vacancies as an efficient electrocatalyst for N2 conversion to NH3 under ambient conditions

Two‐dimensional Boridene Nanosheets for Efficient Electrochemical Nitrogen Fixation under Ambient Conditions

MoO3 Nanosheets for Efficient Electrocatalytic N2 Fixation to NH3

(Invited) Electrochemical Nitrogen Fixation under Ambient Conditions

Monodisperse Cu Cluster-Loaded Defective ZrO 2 Nanofibers for Ambient N 2 Fixation to NH 3

Atomically Dispersed Molybdenum Catalysts for Efficient Ambient Nitrogen Fixation

Ambient Electrochemical N 2 Reduction to NH 3 on Nitrogen and Phosphorus Co‐doped Porous Carbon with Trace Iron in Alkaline Electrolytes

Nanomaterials for the electrochemical nitrogen reduction reaction under ambient conditions

An Amorphous Noble-Metal-Free Electrocatalyst that Enables Nitrogen Fixation under Ambient Conditions.

Ambient Electrosynthesis of Ammonia on a Biomass-Derived Nitrogen-Doped Porous Carbon Electrocatalyst: Contribution of Pyridinic Nitrogen

Molybdenum Carbide Nanodots Enable Efficient Electrocatalytic Nitrogen Fixation under Ambient Conditions

Disordered Au Nanoclusters for Efficient Ammonia Electrosynthesis.