Abstract:Silica aerogels generally exhibit poor mechanical properties, which seriously restrict their commercial use and makes it necessary to reinforce their structures to obtain materials strong enough to withstand mechanical stresses. The incorporation of polymers into silica aerogels is a promising approach due to the enhancement in mechanical strength afforded and the possibility of imparting the hydrophobicity of the polymers to the resulting aerogels. However, the processes typically employed to prepare polymer-reinforced silica aerogels are complex, arduous and costly, requiring multiple washing and soaking steps for the infiltration of the polymer precursors after gelation and supercritical drying. Additionally, diffusion problems can result in heterogeneity in aerogel monoliths due to the use of various cross-linked polymers and the autoclave-limited dimensions of aerogels. In this study, a facile sol–gel route was developed to fabricate a large (500 cm3) polymer–silica aerogel monolith that was stable under atmospheric conditions and suitable for machining. The synthesis of the polymer–silica aerogels began with a facile one-pot reaction involving resorcinol (R), formaldehyde (F), methyltrimethoxysilane (MTMS), and N-(β-aminoethyl)-γ-aminopropyl-trimethoxysilane (AEAPTES), followed by an ambient-pressure drying process. The resulting aerogels were characterised by nitrogen adsorption–desorption, scanning electron microscopy (SEM), contact angle, and thermal conductivity measurements, and the aerogel mechanical properties were evaluated by a unidirectional compression test. The Young's modulus of compression of the aerogels was observed to increase from 3.95 to 34.88 MPa with an increase in the density of the aerogels from 0.14 to 0.26 g cm−3. Simultaneously, the aerogels were observed to be superhydrophobic, with a contact angle as high as 168°, and exhibited low thermal conductivity (0.038 W m−1 K−1) and good absorption for organic liquids, which are critical characteristics for the practical application of aerogels, especially in energy-saving and oil-/chemical-cleanup practices.

Alginate/r-GO/SiO2 aerogels with double catalytic activity sites and high mechanical performance

Flexible, Strong, Multifunctional Graphene Oxide/Silica-Based Composite Aerogels Via a Double-Cross-Linked Network Approach

Self-catalyzed Gelling Synthesis of Aerogels with Inorganic and Organic Nanocomponents for Thermal Insulation and CO 2 Capture

Ultrafine NiO–La2O3–Al2O3 aerogel: a promising catalyst for CH4/CO2 reforming

Biomass-based carbon aerogels prepared by ZnCl 2 -assisted pyrolysis of cellulosic aerogels for selective electrocatalytic CO 2 reduction

High Compression Strength and Thermal Insulation Silica Aerogel Monolith with Scaffold of a Cyclic Olefin Siloxane Co-Oligomer Via Ambient Pressure Drying

Advances in multiple reinforcement strategies and applications for silica aerogel

Synthesis of biomass-based carbon aerogels in energy and sustainability

Ultralight Biomass Aerogels with Multifunctionality and Superelasticity Under Extreme Conditions

A Facile Alkali-Assisted Synthesis Strategy for Hierarchical Porous Carbon Aerogels for Supercapacitors

Boosting Both Electrocatalytic Activity and Durability of Metal Aerogels via Intrinsic Hierarchical Porosity and Continuous Conductive Network Backbone Preservation

Enhancements of thermal insulation and mechanical property of silica aerogel monoliths by mixing graphene oxide

Ultra-high specific surface area spherical FePO x /SiO 2 aerogel with excellent mechanical properties for the highly selective direct oxidation of CH 4 to HCHO

Ambient-pressure drying synthesis of large resorcinol–formaldehyde-reinforced silica aerogels with enhanced mechanical strength and superhydrophobicity

Biomass-Derived Carbon Aerogels for ORR/OER Bifunctional Oxygen Electrodes

Self-assembled porous biomass carbon/RGO/nanocellulose hybrid aerogels for self-supporting supercapacitor electrodes

Robust Silica–Agarose Composite Aerogels with Interpenetrating Network Structure by in Situ Sol–Gel Process

In-situ acid catalysis strategy to achieve rapid ambient pressure drying preparation of aerogels

Low-temperature superelastic, anisotropic, silane-crosslinked sodium alginate aerogel for thermal insulation

Biomass-based carbon aerogels with interconnected pores and controllable Zn–N sites for CO 2 electroreduction

Pd-CoO x nanocomposite aerogels for highly efficient methanol and ethanol oxidation