Effect of Y on the corrosion behavior of Fe22Cr5Al3Mo alloy in 500 °C super-heated steam
Rongrong Sun,Meiyi Yao,Jie Zhang,Haoyu Wang,Xiaodong Lin,Wenhuai Zhang,Yunlong Qiu,Jian Yang,Guoguang Cheng,Jianxin Dong
DOI: https://doi.org/10.1016/j.corsci.2021.110022
IF: 7.72
2022-03-01
Corrosion Science
Abstract:Fe22Cr5Al3Mo-xY (x = 0, 0.15%, mass fraction) alloys were fabricated and corroded in 500 ℃/10.3 MPa super-heated steam using a static autoclave. The results show that the oxide films present a four-layer structure consisting of Fe oxide, Cr oxide, mixed oxide region, and Al oxide from outside to inside. There is α-(Fe, Cr) in Al2O3 layer near the oxide/metal interface. The addition of Y can delay the formation of the large iron oxide particles and increase the ratio of Cr2O3 film thickness to the thickness of the flat oxide film area, thus improving the corrosion resistance of the alloys.
materials science, multidisciplinary,metallurgy & metallurgical engineering