Abstract:Morphologies of the titanium sample were investigated via the Industrial CT system.The systematic research on the conoidal fracture was carried out by the simulation.The periods of three damage zones in which cracks exist are not independent.Effects of stress triaxiality on the crack initiation of three zones are clarified.In order to understand the mechanism of conoidal fracture damage caused by a high-speed fragment-simulating projectile in titanium alloy layer of a composite armor plate composed of titanium- and aluminum-alloy layers, the ballistic interaction process was successfully simulated based on the Tuler–Butcher and GISSMO coupling failure model. The simulated conoidal fracture morphology was in good agreement with the three-dimensional industrial-computed-tomography image. Further, three main damage zones (zones I, II, and III) were identified besides the crater area, which are located respectively near the crater area, at the back of the target plate, and directly below the crater area. Under the high-speed-impact conditions, in zone II, cracks began to form at the end of the period of crack formation in zone I, but crack formation in zone III started before the end of crack formation in zone II. Further, the damage mechanism differed for different stress states. The microcracks in zone I were formed both by void connection and shear deformation. In the formation of zone I, the stress triaxiality ranged from -2.0 to -1.0, and the shear failure mechanism played a dominant role. The microcracks in zone II showed the combined features of shear deformation and void connection, and during the formation process, the stress triaxiality was between 0 and 0.5 with a mixed failure mode. Further, the microcracks in zone III showed obvious characteristics of void connection caused by local melting. During the zone III formation, the triaxiality was 1.0–1.9, and the ductile fracture mechanism was dominant, which also reflects the phenomenon of spallation.

Spallation Affected Fracture Pattern of a Titanium Alloy Plate Subjected to Linear Shaped Charge Jet Penetration

Experimental and Numerical Investigation on Ballistic Penetration Performance of TC4-Al3Ti Layered Composites by Hot Rolling

Numerical simulation of the disk fragment impacting resistance of plate target

Penetration of Disk Fragments Following Impact on Thin Plate

Study of high-speed-impact-induced conoidal fracture of Ti alloy layer in composite armor plate composed of Ti- and Al-alloy layers

Simulation of Fragmentation Characteristics of Projectile Jacket Made of Tungsten Alloy after Penetrating Metal Target Plate Using SPH Method

High Velocity Perforation Simulations of Lightweight Target Plates Using a Modified Johnson-Cook Model

Penetration and Cratering of Steel Target by Jets from Titanium Alloy Shaped Charge Liners

Explosive Separation Properties of Double-hole Charge Structure

The Role of Material Model in the Finite Element Simulation of High-Speed Machining of Ti6Al4V

Numerical simulation on concrete target penetrated by warhead of different titanium alloy shaped charge

Numerical Simulation on Shaped Charge Jet Penetrating Single / Composite Structure of Target Plate

Ductile Fracture of Titanium Alloys in the Dynamic Punch Test

Formation and Penetration Properties of a Shaped Charge with Zr41.2Ti13.8Cu12.5Ni10Be22.5 Liner

Chip Fracture Behavior in the High Speed Machining of Titanium Alloys

Tests and numerical simulation for anti-penetrating behavior of a high strength 7A04-T6 aluminium alloy plate against a blunt projectile's impact

Fracture Behavior of Heat Affected Zone of Laser-Welded Joint for Ti-6al-4v Titanium Alloy: Experimental and Computational Study

Application of the modified Mohr–Coulomb fracture criterion in predicting the ballistic resistance of 2024-T351 aluminum alloy plates impacted by blunt projectiles

Simulation of Spall Fracture Based on Material Point Method

The constitutive behavior of Ti–5Al–3V–2Cr–2Fe under high-velocity impact: Experimental, modeling, and validation

Anisotropic Deformation and Damage of Dual-Phase Ti-6Al-4V under High Strain Rate Loading