Abstract:Zn-exchanged ZSM-5-Al2O3 (ZA) composite-supported Pt/NiMo (NM) sulfided catalysts were prepared using the conventional kneading method and were tested for dehydrocyclization-cracking of soybean oil. The effects of Zn addition on the activity and selectivity of products were investigated under moderate-pressure conditions of 0.5 and 1.0 MPa H2 in the temperature range of 420-580 °C. At the temperature 500 °C and higher, most of the sample soybean oil was converted at both the pressures of 0.5 and 1.0 MPa. At 1.0 MPa and 500 °C, the effects of Zn addition appeared and increased the yields of aromatics, while the catalyst without Zn produced larger amounts of products with more than C18. Further, at 0.5 MPa and 580 °C, the gas formation was inhibited in comparison to the cases of 1.0 MPa and the effects of the Zn addition also appeared and increased the yields of aromatics, while the catalyst without Zn produced larger amounts of products with more than C18. The Pt/NM/Zn(122)ZA test catalyst produced more than 63% of liquid fuels in the range C5-C18, and the yield of aromatics was 13%, the maximum value in the present study. The following reaction routes were proposed. The structure of triglyceride is converted by hydrocracking to three molecules of aliphatic acids and propane on the surface PtNiMo sulfide on Al2O3 support. The converted aliphatic acids are decomposed through decarboxylation to hydrocarbon fragments, which are further decomposed by cracking on the acid sites of the catalyst, the surface of NiMo sulfide, Al2O3, or ZSM-5. Finally, the formed C3 and C4 olefins are transformed to aromatics through the Diels-Alder reaction on the Zn species of ZnZSM-5. On the other hand, although gases were relatively small in amount, aromatic compounds were formed significantly, suggesting that cyclization might directly occur without conversion to gaseous hydrocarbons to some extent.

Catalytic cracking of n -decane over NiO–MoO 3 modified Pt/ZrO 2 –TiO 2 –Al 2 O 3 catalyst with different Al 2 O 3 ratios

Catalytic Decarbonylation Of Stearic Acid To Hydrocarbons Over Activated Carbon-Supported Nickel

Catalytic Cracking of Supercritical N-Dodecane over Meso-Hzsm-5@al-mcm-41 Zeolites

Studies on n-butane isomerization reaction on solid oxide super acid Pt-SO4 2- /ZrO2-Al2O3 catalysts

Effects of Zn Addition into ZSM-5 Zeolite on Dehydrocyclization-Cracking of Soybean Oil Using Hierarchical Zeolite-Al2O3 Composite-Supported Pt/NiMo Sulfided Catalysts

Effect of Si/Al ratio on performance of Pt–Sn-based catalyst supported on ZSM-5 zeolite for n-butane conversion to light olefins

Oleic acid decarboxylation to produce C8-C17 alkanes catalyzed by Pt and Ni on a MOF-derived zirconia

Steam Catalytic Cracking of n-Dodecane to Light Olefins over Phosphorous- and Metal-Modified Nanozeolite Y

Synergetic Regulation of the Microstructure and Acidity of HZSM-5/MCM-41 for Efficient Catalytic Cracking of n-Decane

Synthesis and Performance of Pillared HZSM-5 Nanosheet Zeolites for N-Decane Catalytic Cracking to Produce Light Olefins

The Impact of Support and Reduction Temperature on the Catalytic Activity of Bimetallic Nickel-Zirconium Catalysts in the Hydrocracking Reaction of Algal Oil from Spirulina Platensis

Dehydrocyclization-cracking of soybean oil using β-zeolite-Al2O3 hierarchical composite-supported Pt, Pd, CoMo, and NiMo sulfide catalysts

Synthesis of pillared nanosheet HZSM-5 zeolite films for catalytic cracking of supercritical n-dodecane

Effect of Zn/Al Ratio of Ni/Zno-Al2o3 Catalysts on the Catalytic Deoxygenation of Oleic Acid into Alkane

Catalytic Deoxygenation of C-18 Fatty Acid over Supported Metal Ni Catalysts Promoted by the Basic Sites of ZnAl2O4 Spinel Phase

Alumina-doped Pt/WOx/ZrO2 catalysts for n-heptane isomerization

Catalytic Cracking of Tricyclo [5.2.1.02.6] Decane over HZSM-5 Molecular Sieves

Role of Structure and Acidic Nature on Catalytic Behavior of Nickel Supported H-mordenite, H-ZSM-5, and γ–alumina Catalysts

Isomerization of o-Xylene Over Zeolite-Containing NiMoP/Al2O3Catalysts

Effect of the Cr2O3 Promoter on Pt/WO3-ZrO2 Catalysts for n-Heptane Isomerization

Catalytic Cracking of n-Dodecane to Chemicals: Effect of Variable-Morphological ZSM-5 Zeolites Synthesized Using Various Silica Sources