Effects of Process Parameters on Solidification Structure of A390 Aluminum Alloy Hollow Billet

Kesheng Zuo,Haitao Zhang,Ke Qin,Jianzhong Cui,Qingzhang Chen

DOI: https://doi.org/10.1007/s11663-017-0983-z

2017-01-01

Metallurgical and Materials Transactions B

Abstract:The effects of process parameters on the solidification structure of A390 aluminum alloy hollow billets prepared by direct-chill casting were investigated. The decrease of casting temperature deteriorated the homogeneity and increased the size of primary Si particles in the hollow billet. Although the average size of primary Si particles was not obviously affected by the increase of casting speed, the thickness of Si-depleted layer at the inner wall increased with the higher casting speed. The tensile strength of A390 alloy is a function of the percentage of coarse Si particles (larger than 35 μm) and the average size of primary Si particles. Higher and more stable tensile strength can be received in the hollow billet with the casting temperature of 1050 K (777 °C), because the fine and uniformly distributed primary Si particles were obtained in the hollow billet.