Phase diagram of the Co-Cu-Ti system at 850°C
Honghui Xu,Yong Du,Baiyun Huang,Zhanpeng Jin,Shitong Li,Xiang Zhang
DOI: https://doi.org/10.3139/146.101215
2013-01-01
Abstract:The phase equilibria of the Co-Cu-Ti system at 850°C are investigated using a high-efficiency diffusion couple and six key ternary alloys. The samples are examined by means of optical microscopy, scanning electron microscopy, and electron probe microanalysis. At 850°C, no ternary compound is found. The Ti3Cu phase is a metastable phase. The solubilities of Cu in Ti 2Co, TiCo, TiCo2(c) and TiCo3 were determined to be 8.7, 35.8, 2.1, and 5.4 at.%, respectively. And the solubilities of Co in Ti2Cu, TiCu, Ti3Cu4, and TiCu2 were measured to be 6.6, 0.7, 2.4, and 10.2 at.%, respectively. The following 9 three-phase equilibria are observed: (Ti) + Ti2Co + Ti2Cu, Ti2Co + Ti2Cu + TiCo, Ti2Cu + TiCu + TiCo, TiCu + Ti3Cu4 + TiCo, Ti3Cu4 + TiCu2 + TiCo, TiCu2 + TiCo + (Cu), TiCo + TiCo 2(c) + (Cu), TiCo2(h) + TiCo3 + (Cu). and TiCo3, + (Co) + (Cu). © Carl Hanser Verlag.