Abstract:Phase equilibria in the Co-Fe-Ti ternary system were investigated by means of the equilibrated alloy method with X-ray powder diffraction and electron probe microanalysis. No ternary compounds were found. The experimental results indicated the existence of seven two-phase and one three-phase regions at 600 degrees C, five two-phase and two three-phase regions at 800 degrees C, and six two-phase and two three-phase regions at 950 degrees C. The solubility of Co in TiFe2 was determined to be larger than 54 at.% at all investigated temperatures, and the solubilities of Fe in TiCo3 and Ti2Co showed an appreciable increase with increasing temperature. The three-phase equilibrium in the Ti-rich corner at 800 degrees C was revealed to be ((beta-Ti) + Ti(Fe, Co) + Ti2Co) rather than ((alpha-Ti) + Ti(Fe, Co) + Ti2Co) reported in previous investigations. Based on the experimental data obtained in the present work, three isothermal sections at 600, 800 and 950 degrees C were established.

Experimental Investigation of the Phase Equilibria in the Co–Fe–Ti Ternary System