Abstract:In this paper, 4.5 vol% TiBw/TAl5 composite with columnar network reinforced structure was prepared by pre-sintering and subsequent hot extrusion process. Pre-sintering was conducted at 1100 °C for 0.5 h, and billets were extruded with an extrusion ratio of 10: 1. The extrusion speed was 10 mm/s, and water cooling was adopted. An extrusion temperature range of 925–1100 °C (which covers the phase transition) was used to study the influence of the extrusion temperature on the microstructure evolution and its correlation with strengthening. The results showed that the extrusion temperature played a decisive role in the evolution of the matrix morphology. When the extrusion temperature increased from the (α + β) dual-phase region to the β single-phase region, the microstructure of the composite matrix was mainly composed of elongated α phase and recrystallized α phase. It gradually transformed into a lamellar structure from a high-temperature β phase. TiB whiskers continued to grow and coarsen. The corresponding texture also changed from 〈10−10〉 α//ED component in the dual-phase region to 〈0001〉α//ED and 〈10−11〉 α//ED mixed components, which were related to the high-temperature 〈101〉β//ED component in the β-phase region. Further performance analysis showed that the matrix strength was positively correlated with the content of the lamellar α phase, which increased with the extrusion temperature; however, the strengthening of TiB whiskers was affected by its growth and fragility and displayed a weakening trend. As a result, although the strength of the composite was always better than that of the matrix, its overall strength decreased upon increasing the extrusion temperature, showing the best performance when extruded at 925 °C. The stress of strengthening effect could be accurately estimated by the shear lag model.

Influence of Hot Extrusion Temperature on the Microstructure and the Mechanical Properties of (abow + WO 3 P)/al Hybrid Composites

Influence of Extrusion Temperature on Microstructures and Mechanical Properties of Bi2o3-Coated Al18b4o33 Whisker Reinforced Al Composites

Influence of extrusion temperature on microstructures and mechanical properties of Bi2O3-coated Al18B 4O33 whisker reinforced Al composites

Mechanical Properties and Thermal Shock Performance of W-Y2O3composite Prepared by High-Energy-rate Forging

Effects of heat-treatment on microstructures and mechanical properties of WO3 particle and Al18B4O33 whisker hybrid reinforced Al matrix composites by squeeze casting

Microstructures and Tensile Properties of Hot-Extruded Composite Bi 2 O 3 -Coated ABOw/Al Composite

Mechanical Properties And Microstructure Of Extruded Al2o3p/2024 Al Composites With Different Volume Fraction Reinforcement

Effects of the Extrusion Temperature on the Microstructure and Mechanical Properties of TiBw/Ti6Al4V Composites Fabricated by Pre-Sintering and Canned Extrusion

Effects of Extrusion Temperature on the Properties of a 0.5 wt% GNP/Al Composite in Porthole Die Extrusion

Effect of Extrusion Temperature on the Microstructure and Mechanical Properties of SiCnw/2024Al Composite

Hot deformation behavior and microstructure evolution of Be/2024Al composites

Influence of Hot Extrusion on the Plasticity of SiCW/Al Composites

Microstructure and Mechanical Properties of High Strength Al2o3p/6061al Composites

Influence of Hot Extrusion on Microstructure and Mechanical Properties of Tungsten Based Heavy Alloy

Effect of Znal2o4 Coating on the Compressive Behaviors of Aluminum Borate Whiskers-Reinforced Aluminum Composites at Elevated Temperatures

Hot Deformation Behaviors of Bi2O3-coated Al18B4O33 Whisker Reinforced Aluminum Matrix Composite with High Formability

Low Temperature Extrusion of 6061 Aluminum Matrix Composite Reinforced with SnO2-coated Al18B4O33 Whisker

Temperature influenced microstructure evolution and strengthening of 4.5 vol% TiBw/TA15 composites with columnar-reinforced structure fabricated by pre-sintering and hot extrusion

Improvement of the tensile strength of Al18B4O33w/Al composite at elevated temperatures by change of interfacial state

Study on high temperature strengthening mechanism of TiB 2p/6061Al composite

Research On Extrusion Of Zirconia-Dispersed Alumina Nanocomposite At Elevated Temperature