Abstract:Based on the electrochemical mechanism of steel corrosion, an improved electrochemical model was established to numerically simulate the corrosion of reinforcement in concrete under marine environment. The corrosion potential distribution and current density of corroded reinforcement were deduced from the corresponding micro-environments on the surface of steel bar, including oxygen, chloride ions, temperature and relative humidity. The equilibrium of gaseous oxygen and dissolved oxygen in pore solution was considered in the model. And the diffusion of invasion mediums in cement matrix and interfacial transition zone (ITZ) were also taken into account. The anode and cathode areas on the surface of steel bar was determined by the time-varying distribution of chloride ions rather than a fixed ratio to achieve the self-balance between macrocell and microcell corrosion. The simulation results agree well with the experimental data. The numerical analysis indicates that the growth of environmental chloride ions concentration will enhance the non-uniformity of chloride ions distribution, but does not contribute much to the increase of maximum rust layer thickness on steel surface. In the propagation stage of corrosion, oxygen concentration is a key factor in controlling corrosion reactions compared to chloride ions. Moreover, environment temperature has a positive effect on both the range of active areas on surface of steel rebar and rust layer thickness.

Influence of Mill Scale and Rust Layer on the Corrosion Resistance of Low-Alloy Steel in Simulated Concrete Pore Solution

Long-Term Electrochemical Behavior of Low-Alloy Steel in Simulated Concrete Pore Solution with Chlorides

Effect of Mill Scale on the Long-Term Corrosion Resistance of a Low-Alloy Reinforcing Steel in Concrete Subjected to Chloride Solution

Corrosion resistance of low-alloy steel in concrete subjected to long-term chloride attack: Characterization of surface conditions and rust layers

Effects of Mill Scale and Steel Type on Passivation and Accelerated Corrosion Behavior of Reinforcing Steels in Concrete

Mill Scale and Corrosion Layer at Concrete Surface Cracking

Distribution of Corrosion Products at the Steel-Concrete Interface: Influence of Mill Scale Properties, Reinforcing Steel Type and Corrosion Inducing Method

Influence of Chloride Concentration and Pre-Passivation on the Pitting Corrosion Resistance of Low-Alloy Reinforcing Steel in Simulated Concrete Pore Solution

Influence of Atmospheric Pre-rusting on Corrosion Behavior of Low-Alloy Rebar in Simulated Concrete Pore Solution

Distribution of millscale on corroded steel bars and penetration of steel corrosion products in concrete

Chloride-induced Corrosion Resistance of Low-Alloyed Reinforcement Steels in Two Different Ph Simulated Concrete Solution

Passive Behaviour of New Alloy Corrosion Resistant Steel Cr10Mo1 in Simulating Concrete Pore Solutions with Different Chloride Contents

Influence of Threshold Chloride Concentration on Corrosion Behavior of Low-Alloy Steel Rebar in Concrete Pore Solutions

The Electrochemical Characterization of Rebar Passivation Film in Simulated Concrete Media

Influence of Partial Rust Layer on the Passivation and Chloride-Induced Corrosion of Q235b Steel in the Carbonated Simulated Concrete Pore Solution

Experimental study on passivation and corrosion performances of pre-rusted steel in simulated concrete pore solution

Corrosion of Carbon Steels Subjected to Chloride and Sulfate in Simulated Concrete Pore Solutions with Different Ph

A Self-Balanced Electrochemical Model for Corrosion of Reinforcing Steel Bar in Considering the Micro-Environments in Concrete

Pitting Corrosion Behaviour of New Corrosion-Resistant Reinforcement Bars in Chloride-Containing Concrete Pore Solution

Corrosion Resistance of a Cr-Bearing Low-Alloy Reinforcing Steel: Effect of Surface Condition, Alkaline Solution, and Chloride Content

Influence of Chloride Ions on Corrosion Behavior of Steel Bars in a Simulated Concrete Pore Solution