Abstract:<p>The focus of this work is to characterize the progressive damage and failure behavior of 2.5D woven alumina fiber reinforced silica ceramic matrix thin composite specimen under a planar tension-shear stress state. The tensile and shear stress-strain diagrams in the principal material coordinate system were obtained using the off-axis tension test with the digital image correlation technique. A mesoscale finite element model of the composite material was developed within the framework of continuum damage mechanics. The thickness effect on the macroscopic mechanical response was considered by removing the periodic boundary conditions along the thickness direction. The macroscopic stress-strain response given by the numerical model was validated by the experimental results. The interaction of the planar biaxial tension and shear stresses was taken into account in the model, quantified using a shear contribution coefficient in the modified 3D Hashin failure criterion. The results from the damage evolution analysis indicate that the linear tensile stress-strain response with a brittle fracture characteristic for the on-axis tension specimen is governed by the axial fiber bundle. The nonlinear tensile stress-strain response with the significantly reduced ultimate stress under biaxial tension and shear stress state results from multiple damages with evolution in both axial and transverse fiber bundles. Both the effective tensile modulus and the ultimate tensile strength increase with increasing the thickness of the specimen due to the increase of the fiber volume fraction. The strengthening induced by the size effect is less significant for the specimen under biaxial tension and shear stress state than that for the on-axis tension specimen owing to the involvement of shear response dominated by the matrix of the material. The results of this study provide new insight into the failure of 2.5D woven ceramic-based composite material, which contributes to the optimal design of the reusable thermal protection system structure.</p>

A mesoscopic model of mechanical erosion for the characterization of ablation behavior of C/C woven composites

Mesoscopic modeling of mechanical erosion for the ablation-erosion behavior of 3D C/C composites

Progressive failure analysis of 2D woven composites at the meso-micro scale

Continuum Damage Modeling and Progressive Failure Analysis of Carbon Fiber/epoxy Composite Pressure Vessel

Analysis of thermochemical ablation and mechanical erosion of C/C composites based on macro-meso-scale numerical simulation methods

Numerical Simulation of C/C Composites Coupled Thermo-Mechanical Field under the Condition of High Temperatures and Ablation

Ablation and mechanical behaviour of C/C composites under an oxyacetylene flame and tensile loading environment

Numerical analyses of ablative behavior of C/C composite materials

Tensile‐after‐ablation progressive damage and the failure mechanism of 2.5D woven composites with crack pores

Modeling ablative behavior and thermal response of carbon/carbon composites

Starting from essence to reveal the ablation behavior and mechanism of 3D PyC Cf/ZrC-SiC composite

Micromechanical Modeling Tensile and Fatigue Behavior of Fiber-Reinforced Ceramic-Matrix Composites Considering Matrix Fragmentation and Closure

Development of a Numerical Material Model for Axial Crushing Mechanical Characterization of Woven CFRP Composites

Erosion in a Melt-Infiltrated SiC/SiC Ceramic Matrix Composite

A new progressive damage model for predicting the tensile behavior of the three-dimensional woven carbon/carbon composites using micromechanics method

Experimental and numerical investigation of progressive damage and failure behavior for 2.5D woven alumina fiber/silica matrix composites under a complex in-plane stress state

Meso-scale modeling and damage analysis of carbon/epoxy woven fabric composite under in-plane tension and compression loadings

Modeling the high temperature behavior of all-composite, corrugated-core sandwich panels undergoing ablation

A meso-scale stochastic model for tensile behavior of 2D woven ceramic composites considering void defects and stacking mode

Experimental and numerical studies on low-velocity impact of laminated C/SiC structures

A temperature-dependent constitutive model for fiber-reinforced ceramic matrix composites and structural stress analysis