Precipitation of calcium–alumino–silicate–hydrate gels: The role of the internal stress

Cheng Zhao,Wei Zhou,Qi Zhou,Yao Zhang,Han Liu,Gaurav Sant,Xinghong Liu,Lijie Guo,Mathieu Bauchy

DOI: https://doi.org/10.1063/5.0010476

IF: 4.304

2020-07-07

The Journal of Chemical Physics

Abstract:Concrete gains its strength from the precipitation of a calcium–alumino–silicate–hydrate (C–A–S–H) colloidal gel, which acts as its binding phase. However, despite concrete's ubiquity in the building environment, the atomic-scale mechanism of C–A–S–H precipitation is still unclear. Here, we use reactive molecular dynamics simulations to model the early-age precipitation of a C–A–S–H gel. We find that, upon gelation, silicate and aluminate precursors condensate and polymerize to form an aluminosilicate gel network. Notably, we demonstrate that the gelation reaction is driven by the existence of a mismatch of atomic-level internal stress between Si and Al polytopes, which are initially experiencing some local tension and compression, respectively. The polymerization of Si and Al polytopes enables the release of these competitive stresses.

chemistry, physical,physics, atomic, molecular & chemical

What problem does this paper attempt to address?

### Problems the paper attempts to solve

This paper aims to explore the mechanism of the role of internal stress during the precipitation process of calcium - aluminum - silicate - hydrate (C - A - S - H) gels. Specifically, the researchers used reactive molecular dynamics simulations to study the atomic structure changes of C - A - S - H gels during the early precipitation process and revealed the following points:

1. **Condensation and polymerization of silicate and aluminate precursors**:
- It was found that during the gelation process, silicate and aluminate precursors gradually condense and polymerize to form an aluminosilicate gel network.

2. **Mismatch of internal stress**:
- Silicon and aluminum polyhedra experience local tension and compression respectively in the initial state. This mismatch of internal stress is a key factor driving the gelation reaction.

3. **Stress - release mechanism**:
- The condensation and polymerization of silicon and aluminum polyhedra help to release these competing internal stresses, thus promoting the sol - gel reaction at the atomic level.

### Key findings

- **Polymerization of silicate and aluminate**:
- The simulation results show that as gelation progresses, silicate and aluminate monomers gradually condense and form aluminosilicate chains and ring - like structures.

- **Changes in internal stress**:
- In the initial state, silicon atoms are in a state of local tension, while aluminum atoms are in a state of local compression. As gelation progresses, the stress of silicon atoms decreases slightly, while the stress of aluminum atoms increases significantly.

- **Reduction in stress matching**:
- During the gelation process, the stress mismatch between silicon and aluminum atoms decreases rapidly and eventually becomes negligible. This indicates that gelation provides a way for silicon and aluminum atoms to release their internal stress through inter - connection.

### Conclusion

This study, through reactive molecular dynamics simulations, reveals the mechanism of the role of internal stress during the early precipitation process of C - A - S - H gels. The research results show that the stress mismatch between silicon and aluminum polyhedra is an important factor driving the gelation reaction, and the release of this stress is achieved through the condensation and polymerization of silicon and aluminum polyhedra. This finding is of great significance for understanding the formation mechanism of C - A - S - H gels and is helpful for the development of new low - carbon - footprint cementitious materials.