Structurally Disordered Phosphorus-Doped Pt as a Highly Active Electrocatalyst for an Oxygen Reduction Reaction
Bang-An Lu,Lin-Fan Shen,Jia Liu,Qinghua Zhang,Li-Yang Wan,David J. Morris,Rui-Xiang Wang,Zhi-You Zhou,Gen Li,Tian Sheng,Lin Gu,Peng Zhang,Na Tian,Shi-Gang Sun
DOI: https://doi.org/10.1021/acscatal.0c03137
IF: 12.9
2020-12-21
ACS Catalysis
Abstract:The application of Pt alloy catalysts for oxygen reduction reactions (ORRs) in proton-exchange membrane fuel cells is severely impeded by base metal leaching, since the produced metal ions can result in the degradation of a Nafion membrane by replacing H<sup>+</sup> and inducing a Fenton reaction. Doping Pt with nonmetal elements can significantly mitigate such problems due to the relative harmlessness of the corrosion products of anions. Herein, we developed a phosphorus-doping strategy, which can greatly boost the ORR performance of Pt. Phosphorus was introduced into the near-surface of commercial Pt/C (denoted as P<sub>NS</sub>-Pt/C) via a surfactant-free method. High-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and X-ray photoelectron spectrum (XPS) tests indicate that the introduction of phosphorus induced distortion of the Pt lattice and the downshift of the d-band center. In situ electrochemical Fourier transform infrared (FTIR) spectroscopy with adsorbed CO as a molecule probe further revealed that the introduction of phosphorus can lower the adsorption ability. The ORR mass activity of P<sub>NS</sub>-Pt/C is as high as 1.00 mA μg<sub>Pt</sub><sup>–1</sup>@0.90 V, which is enhanced by 7 times in comparison with the initial Pt/C catalyst. Meanwhile, the durability is also enhanced. After 10 000 potential cycles, P<sub>NS</sub>-Pt/C only lost 14% of the ORR mass activity, while Pt/C lost 51%. More importantly, a H<sub>2</sub>–air fuel cell with a P<sub>NS</sub>-Pt/C cathode achieves a power density of 1.06 W cm<sup>–2</sup> at a current density of 2.0 A cm<sup>–2</sup> with a low Pt loading of 0.15 mg cm<sup>–2</sup>. The current density at 0.60 V (practical working potential) is 1.54 A cm<sup>–2</sup>, 2 times higher than that of commercial Pt/C. Density functional theory (DFT) calculations indicate that near-surface phosphorus doping can induce the distortion of the Pt surface, on which some concave Pt sites have optimal binding energy of OH for the ORR. Furthermore, this phosphorus-doping strategy is also valid for a PtNi alloy catalyst to further boost the ORR performance.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.0c03137?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.0c03137</a>.Experimental details; XRD refined results; in situ FTIR spectra; electrochemical tests; CV curves; and tables for performance comparison (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.0c03137/suppl_file/cs0c03137_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, physical