Effect of strain on DRX of 7050 aluminum alloy during extrusion at high temperature

Zhu Danyang,Zhen Liang,Hu Wenhao,Chen Junzhou,Cui Yuexian,Shao Wenzhu

IF: 6.318

2007-01-01

Rare Metals

Abstract:Extrusion experiments with different filling contents at the temperature of 440 degrees C were conducted for solution treated 7050 aluminum alloy. The microstructure of typical regions with different filler contents were described qualitatively and charactenized quantitatively by electron backseattered diffraction technique (EBSD) and TEM. Fraction of deformed structure decrease continuously since epsilon = 0.72. Second phase particles distribute dispersively and interact with dislocations when epsilon = 0.66, which delays the occurrence of DRX. As the strain increases I particles dissolve into the matrix, and their number reduces rapidly. The influence of particles on dislocation accumulation is impaired, so dislocations accumulate on the subgrain boundaries continuously, and lead to the transformation of subgrain boundaries into high angle grain boundaries (HAGBs). The continuous dynamic recrystallization (CDRX) occurrs at the strain of 0.81 similar to 0.85. At epsilon = 0.92, CDRX convert rapidly with the increase of HAGBs fraction. But the size of CDRX grains is deduced to be minimum 3.3 mu m by theoretical analysis, and it is obtained from experimental result that the maximal size of CDRX is 5.3 mu m.