Abstract:Exploring an efficient and pollution-free hydrogen evolution reaction (HER) electrocatalyst based on the combination of rare-earth metal and nonnoble metal is of significant importance. However, successfully achieving such a goal remains highly challenging. Herein, a nanosheet comprising a MoO2-CeF3 heterojunction (MoO2-CeF3/NF) is successfully prepared via a three-step method. (1) Growth of hexahedral nickel hydroxide [Ni(OH)(2)] on a 3D nickel foam (NF) as the scaffold. (2) In situ hydrothermal growth of a precursor nanosheet structure on the scaffold. (3) Calcination treatment at 450 degrees C in the presence of hydrogen. Herein, the electron redistribution at the heterointerface of CeF3 and MoO2 is a contributing factor toward enhanced HER activity. Appropriate introduction of CeF3 can enlarge the size of nanosheets, increase numerous active sites, increase the catalytic durability of the material, and change electron distribution on the MoO2 interface; all of the above improve HER activity. Because of its interfacial nanosheet structure, MoO2-CeF3/NF demonstrates pre-eminent HER capability in both alkaline (1.0 M KOH) and acidic (0.5 M H2SO4) electrolytes, with extremely small overpotentials of 18 and 42 mV at 10 mA cm(-2), respectively. This is obviously lower than the overpotential of Pt/C in alkaline media (27 mV), and it is also close to the overpotential of Pt/C in acidic media (41 mV), at the same current density. More importantly, MoO2-CeF3/NF displays a better HER activity than Pt/C at a current density of >112 mA cm(-2) in both alkaline and acidic electrolytes. This work offers a novel strategy toward high-performance hydrogen production by designing a transition metal oxide and rare-earth metal heterojunction.

Interface Engineering of a CeO2-Cu3P Nanoarray for Efficient Alkaline Hydrogen Evolution.

Pd/CeO2 Interface with Abundant Oxygen Vacancies for Alkaline Hydrogen Evolution/Oxidation Reaction

Efficient Hydrogen Evolution Electrocatalysis at Alkaline Ph by Interface Engineering of Ni2P-CeO2

Simultaneous Interfacial Chemistry and Inner Helmholtz Plane Regulation for Superior Alkaline Hydrogen Evolution

Strongly Coupled Hollow-Oxide/phosphide Hybrid Coated with Nitrogen-Doped Carbon As Highly Efficient Electrocatalysts in Alkaline for Hydrogen Evolution Reaction

Interface engineering of the Ni(OH)2–Ni3N nanoarray heterostructure for the alkaline hydrogen evolution reaction

An Ultrafine Platinum-Cobalt Alloy Decorated Cobalt Nanowire Array with Superb Activity Toward Alkaline Hydrogen Evolution

Generation of Dual Anion Vacancies on CeO2/Co4N interfaces to Facilitate Hydrogen Evolution Reaction in Alkaline Solution

Interfacial Engineering of a MoO2-CeF3 Heterostructure As a High-Performance Hydrogen Evolution Reaction Catalyst in Both Alkaline and Acidic Solutions

Porous CeO2/Ni-Cu composite catalyst for electrocatalytic hydrogen evolution in alkaline medium

F-CuCoP nanoarrays decorated with Ni(OH) 2 nanoparticles for boosted electrocatalytic hydrogen evolution reaction

Flower-like CeO2-supported Small-Sized Ru Nanoparticle Hybrids for Highly Efficient Alkaline Hydrogen Evolution: Roles of Interfacial Effects

A cobalt-phosphorus nanoparticle decorated N-doped carbon nanosheet array for efficient and durable hydrogen evolution at alkaline pH

Highly Efficient and Self-Standing Nanoporous NiO/Al3Ni2 Electrocatalyst for Hydrogen Evolution Reaction

Superior Alkaline Hydrogen Evolution Electrocatalysis Enabled By An Ultrafine Ptni Nanoparticle-Decorated Ni Nanoarray With Ultralow Pt Loading

Coupling NiCo Alloy and CeO 2 to Enhance Electrocatalytic Hydrogen Evolution in Alkaline Solution

A 3D porous Ni-CeO2 nanosheet array as a highly efficient electrocatalyst toward alkaline hydrogen evolution

Interfacial Engineering Regulated by CeOx to Boost Efficiently Alkaline Overall Water Splitting and Acidic Hydrogen Evolution Reaction

Nanoporous cobalt-doped AlNi3/NiO architecture for high performing hydrogen evolution at high current densities

CeO x -Decorated NiFe-Layered Double Hydroxide for Efficient Alkaline Hydrogen Evolution by Oxygen Vacancy Engineering.

3D hierarchical nanostructured NiCo-LDH/Cu electrode for efficient alkaline hydrogen evolution