Fuel Cladding Chemical Interactions for MOX Fuel in Fast Reactors
Jie Gao,Shasha Lv,Zhangshun Ruan,Jingjing Liao,Dongyue Chen,Xiaogang Fu,Zhengcao Li
DOI: https://doi.org/10.1016/j.nucengdes.2024.113208
IF: 1.7
2024-01-01
Nuclear Engineering and Design
Abstract:An important factor in determining the integrity and lifetime of fuel assemblies in fast breed reactors is the fuel-cladding chemical interaction (FCCI) between MOX fuel and stainless steel cladding. This FCCI has been widely investigated through numerous in-pile and out-pile tests. Fission products (caesium, tellurium, iodine, etc.) and in-pile fuel and irradiation parameters (initial stoichiometric ratio of MOX fuel, burn-up, and cladding temperature, etc.) play an important role in the FCCI mechanism and corrosion severity of the cladding, leading to complex surface and matrix corrosion conditions. Cs- and Te-induced corrosion dominate at high and low oxygen potentials, respectively, leading to severe corrosion associated with the cladding components. However, a coupling effect of both elements is present at specific oxygen potentials. The temperature, burn-up and initial stoichiometric ratio of the fuel determine the oxygen potential at the inner surface of cladding, thus affecting the type and depth of corrosion caused by fission products. Based on these affecting factors, several prediction models applicable to different conditions have been proposed, among which the Japanese model and HEDL model are considered suitable for high and low oxygen potentials, respectively. Nevertheless, both models neglect the impacts of cladding components and properties. Finally, the differences between out-pile simulations and in-pile irradiation experiments are discussed, which need to be emphasized when analysing the experimental results.