Rational Use and Reuse of Nafion 212 Membrane in Vanadium Flow Batteries

Ying Zhou,Lihong Yu,Jianshe Wang,Le Liu,Feng Liang,Jingyu Xi

DOI: https://doi.org/10.1039/c7ra00294g

IF: 4.036

2017-01-01

RSC Advances

Abstract:A rational use of Nafion membrane can achieve superior VFB performance, and Nafion membrane can be reused in VFB.

What problem does this paper attempt to address?

Nafion/SiO2 Hybrid Membrane for Vanadium Redox Flow Battery

Jingyu Xi,Zenghua Wu,Xinping Qiu,Liquan Chen

DOI: https://doi.org/10.1016/j.jpowsour.2007.01.069

IF: 9.2

2007-01-01

Journal of Power Sources

Abstract:Sol–gel derived Nafion/SiO2 hybrid membrane is prepared and employed as the separator for vanadium redox flow battery (VRB) to evaluate the vanadium ions permeability and cell performance. Nafion/SiO2 hybrid membrane shows nearly the same ion exchange capacity (IEC) and proton conductivity as pristine Nafion 117 membrane. ICP-AES analysis reveals that Nafion/SiO2 hybrid membrane exhibits dramatically lower vanadium ions permeability compared with Nafion membrane. The VRB with Nafion/SiO2 hybrid membrane presents a higher coulombic and energy efficiencies over the entire range of current densities (10–80 mA cm−2), especially at relative lower current densities (<30 mA cm−2), and a lower self-discharge rate compared with the Nafion system. The performance of VRB with Nafion/SiO2 hybrid membrane can be maintained after more than 100 cycles at a charge–discharge current density of 60 mA cm−2. The experimental results suggest that the Nafion/SiO2 hybrid membrane approach is a promising strategy to overcome the vanadium ions crossover in VRB.
A cost-effective nafion/lignin composite membrane with low vanadium ion permeation for high performance vanadium redox flow battery

Jiaye Ye,Du Yuan,Mei Ding,Yong Long,Ting Long,Lidong Sun,Chuankun Jia

DOI: https://doi.org/10.1016/j.jpowsour.2020.229023

IF: 9.2

2021-01-01

Journal of Power Sources

Abstract:Here we report an eco-friendly Nafion/lignin composite membrane with excellent performance for vanadium redox flow battery (VRFB). Through facile solution casting, the Nafion/lignin composite membrane presents the merits of high conductivity and low vanadium ions permeability. Under high current density (120 mA cm−2), the VRFB single cell with the optimized Nafion/lignin composite membrane exhibits superior performance metrics to commercial counterpart: high Coulombic efficiency (~97.4%) and energy efficiency (~82.7%), and prominent cyclability with slower capacity decay for ~52.8% capacity retention after 1000 cycles (vs. Nafion 212 membrane ~34.8% after only 150 cycles). More importantly, compared with the pristine Nafion 212 membrane, the cost of the composite membrane is reduced sharply by reducing the usage amount of Nafion polymer, while maintaining the membrane stability. Thus, the Nafion/lignin composite membrane is one of the competitive candidates for VRFB towards commercialization.

energy & fuels,materials science, multidisciplinary,electrochemistry,chemistry, physical
A Comparative Study of Nafion Series Membranes for Vanadium Redox Flow Batteries

Bo Jiang,Lantao Wu,Lihong Yu,Xinping Qiu,Jingyu Xi

DOI: https://doi.org/10.1016/j.memsci.2016.03.007

IF: 9.5

2016-01-01

Journal of Membrane Science

Abstract:In this study, a series of the commercial Nafion membranes (equivalent weight of 1100gmol−1) with thickness of 50μm (Nafion 112), 88μm (Nafion 1135), 125μm (Nafion 115), and 175μm (Nafion 117) are selected to investigate the thickness impact of Nafion on the performance of vanadium redox flow battery (VRFB). VRFBs are evaluated at a broad current density range from 40 to 320mAcm−2. The self-discharge process, cell efficiencies, electrolyte utilization, and long-term cycling stability of VRFBs based on various Nafion membranes are compared comprehensively. Owing to the good balance between vanadium ions permeability and membrane resistance, Nafion 115 membrane presents the highest energy efficiency and electrolytes utilization at current density from 120 to 240mAcm−2. A simple and powerful online monitoring system is developed to monitor the electrolyte imbalance process during the cycle-life test of VRFB. The capacity fading mechanism of VRFBs with different Nafion membranes is also discussed.
Performance of a vanadium redox flow battery with a VANADion membrane

X.L. Zhou,T.S. Zhao,L. An,Y.K. Zeng,X.B. Zhu

DOI: https://doi.org/10.1016/j.apenergy.2016.08.001

IF: 11.2

2016-10-01

Applied Energy

Abstract:Conventional vanadium redox flow batteries (VRFBs) using Nafion 115 suffered from issues associated with high ohmic resistance and high capital cost. In this work, we report a commercial membrane (VANADion), consisting of a porous layer and a dense Nafion layer, as a promising alternative to Nafion 115. In the dual-layer structure, the porous layer (∼210μm) can offer a high ionic conductivity and the dense Nafion layer (∼20μm) can depress the convective flow of electrolyte through the membrane. By comparing with the conventional Nafion 115 in a VRFB, it is found that the change from the conventional Nafion 115 to the composite one results in an increase in the energy efficiency from 71.3% to 76.2% and an increase in the electrolyte utilization from 54.1% to 68.4% at a current density of as high as 240mAcm−2. In addition, although two batteries show the comparable cycling performance at current densities ranging from 80mAcm−2 to 240mAcm−2, the composite membrane is estimated to be significantly cheaper than the conventional Nafion 115 due to the fact that the porous layer is rather cost-effective and the dense Nafion layer is rather thin. The impressive combination of desirable performance and low cost makes this composite membrane highly promising in the VRFB applications.

energy & fuels,engineering, chemical
Nafion/Organic Silica Hybrid Membrane for Vanadium Redox Flow Battery

Teng Xiangguo,Zhao Yongtao,Xi Jingyu,Wu Zenghua,Qiu Xinping,Chen Liquan

DOI: https://doi.org/10.3321/j.issn:0567-7351.2009.06.003

2009-01-01

Acta Chimica Sinica

Abstract:Nafion/organic silica hybrid membrane was prepared via an in situ sot-gel reaction method and the ion exchange capacity (IEC), conductivity and water transport rate of the hybrid membrane were measured. Results indicate that compared with Nafion membrane, the hybrid membrane can efficiently block water transfer across the membrane. The average coulombic efficiency and energy efficiency of the VRB with the Nafion/organic silica membrane were all remarkably increased. Furthermore, the Nafion/organic silica 2 hybrid membrane is very stable for more than 80 charge-discharge cycles at current density of 60 mA.cm(-2). Results show that the Nafion/organic silica membrane is a novel hybrid membrane and applicable to VRB.
A Recast Nafion/graphene Oxide Composite Membrane for Advanced Vanadium Redox Flow Batteries

Lihong Yu,Feng Lin,Ling Xu,Jingyu Xi

DOI: https://doi.org/10.1039/c5ra24317c

IF: 4.036

2016-01-01

RSC Advances

Abstract:GO nanosheets in Nafion effectively block the crossover of vanadium ions while hydrogen bonds between GO and Nafion increase the mechanical stability, significantly improving the efficiency and cyclability in a rNafion/GO membrane based VRFB.
A high performance polytetrafluoroethene/Nafion composite membrane for vanadium redox flow battery application

Xiangguo Teng,Jicui Dai,Jing Su,Yongming Zhu,Haiping Liu,Zhiguang Song

DOI: https://doi.org/10.1016/j.jpowsour.2013.03.177

IF: 9.2

2013-01-01

Journal of Power Sources

Abstract:To reduce the consumption and improve the performance of Nafion, a thin polytetrafluoroethene (PTFE)/Nafion (P/N) composite membrane for vanadium redox flow battery (VRB) application was prepared by impregnating porous PTFE membrane with Nafion solution. The P/N membrane is almost as transparent as commercial Nafion 212 (N212) membrane, which can be easily cut into any desired shape and size. SEM and AFM analyses prove that the Nafion resin uniformly filled into the micro-pores of porous PTFE membrane. Results also show that the swelling ratio, Nafion consumption, water transport and vanadium ions permeability of P/N membrane are smaller than that of N212. The VRB with P/N membrane has higher coulombic efficiency, voltage efficiency and energy efficiency than that of N212 at all tested current densities, and the average EE of VRB with P/N membrane is 5.2% higher than that of the VRB with N212 at current densities from 40 to 70 mA cm−2. Furthermore, owing to the lower vanadium ions permeability, the self-discharge of the VRB with P/N membrane is much slower than that of the VRB with N212, and 45 cycles charge–discharge test proves that the P/N membrane is very stable and has better capacity retention ability than that of N212.
Surface-Modified Approach to Fabricate Nafion Membranes Covalently Bonded with Polyhedral Oligosilsesquioxane for Vanadium Redox Flow Batteries

Hongli An,Run Zhang,Wenhao Li,Pan Li,Huidong Qian,Hui Yang

DOI: https://doi.org/10.1021/acsami.1c20627

2022-02-01

Abstract:An aminopropyl isobutyl polyhedral oligosilsesquioxane (NH2-POSS) surface-modified Nafion membrane has been designed by chemical grafting for vanadium redox flow batteries (VRFBs). NH2-POSS is a cage-like macromer consisting of an inorganic Si8O12 core surrounded by seven inert isobutyl groups and one active aminopropyl group. The sulfonic acid groups on the surface of Nafion can be activated by 1,1-carbonyldiimidazole for further modification with NH2-POSS. Fourier transform infrared spectroscopy (FT-IR) and X-ray photoelectron spectroscopy (XPS) prove that NH2-POSS has been successfully grafted on the surface of a Nafion 115 membrane. Although the proton conductivity decreases slightly, the organic-inorganic hybrid membranes display enhanced ion selectivity and excellent dimensional stability with lower water uptake and swelling ratio than Nafion 115. Moreover, two-dimensional-grazing incidence X-ray diffraction (2D-GIXRD) reveals that the introduction of NH2-POSS forms a POSS layer on the surface of the membrane and narrows the space of Nafion clusters, which helps to block VO2+ permeation. A VRFB with the surface-modified Nafion membrane displays an outstanding performance with an average Coulombic efficiency (CE) of 98.7% and energy efficiency (EE) of 84.5% at a current density of 80 mA cm-2, superior to those of the Nafion 115 membrane (CE = 95.7%, EE = 81.7%). Furthermore, the cell holds a high capacity retention of 49.2% after 1000 charge-discharge cycles, in contrast to that of 41.9% for the cell with Nafion 115 after only 200 cycles. The results suggest that the surface-modified hybrid membrane is a promising strategy to overcome the vanadium ion crossover in VRFBs.

materials science, multidisciplinary,nanoscience & nanotechnology
Advanced Nafion hybrid membranes with fast proton transport channels toward high-performance vanadium redox flow battery

Dezhu Zhang,Li Xin,Yongsheng Xia,Liheng Dai,Kai Qu,Kang Huang,Yiqun Fan,Zhi Xu

DOI: https://doi.org/10.1016/j.memsci.2020.119047

IF: 9.5

2021-04-01

Journal of Membrane Science

Abstract:The development of high-performance ion exchange membranes to break the trade-off between ion selectivity and conductivity is always a great challenge for the vanadium redox flow battery (VRFB). Herein, a hybrid membrane was successfully prepared via the solution casting method. The UiO-66-SO3H was embedded in Nafion matrix, acting as an effective barrier for vanadium ions to realize enhanced ion selectivity. At the same time, besides the intrinsic proton cluster channels in Nafion, two types of additional proton transport channels formed in the membranes, which further improved the conductivity of the membranes. Consequently, the VRFB with an optimized hybrid membrane exhibited enhanced voltage efficiency (VEs: 91.5-78.4%) and outstanding energy efficiency (EEs: 86.0-76.1%) compared with the one with recasting Nafion membrane (rNf) (VEs: 86.9-69.0%, EEs: 80.3-66.0%) at 80–220 mA cm-2. The efficiency kept stable for 1000 cycles in the long-term cycling tests, and the discharge capacity decay rate of the VRFB with the hybrid membrane is only 0.13% per cycle, which is in obvious contrast to the one with rNf (0.73% per cycle). In addition, the electrolyte utilization rate of the VRFB assembled with the hybrid membrane was much higher than that of the one with rNf.

engineering, chemical,polymer science
Nafion/organically modified silicate hybrids membrane for vanadium redox flow battery

Teng Xiangguo,Zhao Yongtao,Xi Jingyu,Wu Zenghua,Qiu Xinping,Chen Liquan

DOI: https://doi.org/10.1016/j.jpowsour.2008.12.040

IF: 9.2

2009-01-01

Journal of Power Sources

Abstract:In our previous work, Nafion/SiO2 hybrid membrane was prepared via in situ sol–gel method and used for the vanadium redox flow battery (VRB) system. The VRB with modified Nafion membrane has shown great advantages over that of the VRB with Nafion membrane. In this work, a novel Nafion/organically modified silicate (ORMOSIL) hybrids membrane was prepared via in situ sol–gel reactions for mixtures of tetraethoxysilane (TEOS) and diethoxydimethylsilane (DEDMS). The primary properties of Nafion/ORMOSIL hybrids membrane were measured and compared with Nafion and Nafion/SiO2 hybrid membrane. The permeability of vanadium ions through the Nafion/ORMOSIL hybrids membrane was measured using an UV–vis spectrophotometer. The results indicate that the hybrids membrane has a dramatic reduction in crossover of vanadium ions compared with Nafion membrane. Fourier transform infrared spectra (FT-IR) analysis of the hybrids membrane reveals that the ORMOSIL phase is well formed within hybrids membrane. Cell tests identify that the VRB with Nafion/ORMOSIL hybrids membrane presents a higher coulombic efficiency (CE) and energy efficiency (EE) compared with that of the VRB with Nafion and Nafion/SiO2 hybrid membrane. The highest EE of the VRB with Nafion/ORMOSIL hybrids membrane is 87.4% at 20mAcm−2, while the EE of VRB with Nafion and the EE of VRB with Nafion/SiO2 hybrid membrane are only 73.8% and 79.9% at the same current density. The CE and EE of VRB with Nafion/ORMOSIL hybrids membrane is nearly no decay after cycling more than 100 times (60mAcm−2), which proves the Nafion/ORMOSIL hybrids membrane possesses high chemical stability during long charge–discharge process under strong acid solutions. The self-discharge rate of the VRB with Nafion/ORMOSIL hybrids membrane is the slowest among the VRB with Nafion, Nafion/SiO2 and Nafion/ORMOSIL membrane, which further proves the excellent vanadium ions blocking characteristic of the prepared hybrids membrane.
Membrane Development for Vanadium Redox Flow Batteries

Birgit Schwenzer,Jianlu Zhang,Soowhan Kim,Liyu Li,Jun Liu,Zhenguo Yang

DOI: https://doi.org/10.1002/cssc.201100068

IF: 8.4

2011-10-06

ChemSusChem

Abstract:Large-scale energy storage has become the main bottleneck for increasing the percentage of renewable energy in our electricity grids. Redox flow batteries are considered to be among the best options for electricity storage in the megawatt range and large demonstration systems have already been installed. Although the full technological potential of these systems has not been reached yet, currently the main problem hindering more widespread commercialization is the high cost of redox flow batteries. Nafion, as the preferred membrane material, is responsible for about 11% of the overall cost of a 1 MW/8 MWh system. Therefore, in recent years two main membrane related research threads have emerged: 1) chemical and physical modification of Nafion membranes to optimize their properties with regard to vanadium redox flow battery (VRFB) application; and 2) replacement of the Nafion membranes with different, less expensive materials. This review summarizes the underlying basic scientific issues associated with membrane use in VRFBs and presents an overview of membrane-related research approaches aimed at improving the efficiency of VRFBs and making the technology cost-competitive. Promising research strategies and materials are identified and suggestions are provided on how materials issues could be overcome.

chemistry, multidisciplinary,green & sustainable science & technology
Nafion/organic Silica Modified TiO2 Composite Membrane for Vanadium Redox Flow Battery Via in Situ Sol–gel Reactions

Xiangguo Teng,Yongtao Zhao,Jingyu Xi,Zenghua Wu,Xinping Qiu,Liquan Chen

DOI: https://doi.org/10.1016/j.memsci.2009.05.051

IF: 9.5

2009-01-01

Journal of Membrane Science

Abstract:To improve the selectivity of Nafion membrane, reduce the crossover of vanadium ions and decrease water transfer across the membranes used in VRB systems, the sol–gel method was employed to obtain a composite membrane of Nafion/organic silica modified TiO2 (Nafion/Si/Ti hybrid membrane). The preparation technique and characteristics of the composite membrane were described. The water transfer and the permeability of vanadium ions were also measured. Results showed that crossover of vanadium ions and water transfer across the membrane for the composite membrane have a remarkable decrease comparing with the unmodified Nafion membrane. It has been confirmed by EDX and FT-IR analysis of the modified membrane that the Si and Ti elements distributed uniformly in the prepared membrane. As a result, the coulombic efficiency of the VRB single cell with modified Nafion membrane was higher than that of the VRB single cell with pristine Nafion membrane. The ion exchange capacity (IEC), the area resistance and the water uptake of the composite membrane were also evaluated. Furthermore, the open circuit voltage (OCV) of the VRB with modified and unmodified Nafion membrane has been carried out and cycle performance of the VRB with modified membrane proves that it has high stability in strong acid condition.
Solution casting Nafion/polytetrafluoroethylene membrane for vanadium redox flow battery application

Xiangguo Teng,Cui Sun,Jicui Dai,Haiping Liu,Jing Su,Faqiang Li

DOI: https://doi.org/10.1016/j.electacta.2012.10.093

IF: 6.6

2013-01-01

Electrochimica Acta

Abstract:Solution casting method was adopted using Nafion and polytetrafluoroethylene (PTFE) solution to prepare Nafion/PTFE blend membranes for vanadium redox flow battery application. The physicochemical properties of the membranes were characterized by using water uptake, Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and thermal analysis (TA). The electrochemical properties of the membranes were examined by using electrochemical impedance spectroscopy (EIS) and single cell test. Despite the high miscibility of PTFE with Nafion, the addition of hydrophobic PTFE reduces the water uptake, ion exchange capacity (IEC) and conductivity of blend membranes. But PTFE can increase the crystallinity, thermal stability of Nafion/PTFE membranes and reduce the vanadium permeability. The blend membrane with PTFE (30wt%, N0.7P0.3) was chosen and investigated for VRB single cell test. The energy efficiency of this VRB with N0.7P0.3 membrane was 85.1% at current density of 50mAcm−2, which was superior to that of recast Nafion (r-Nafion) membrane (80.5%). Self-discharge test shows that the decay of open circuit potential of N0.7P0.3 membrane is much lower than that of r-Nafion membrane. More than 50 cycles charge–discharge test proved that the N0.7P0.3 membrane possesses high stability in long time running. Chemical stabilities of the chosen N0.7P0.3 membrane are further proved by soaking the membrane for 3 weeks in highly oxidative V(V) solution. All results suggest that the addition of PTFE is a simple and effective way to improve the performance of Nafion for VRB application.
Self-Assembled Polyelectrolyte Multilayer Modified Nafion Membrane with Suppressed Vanadium Ion Crossover for Vanadium Redox Flow Batteries

Jingyu Xi,Zenghua Wu,Xiangguo Teng,Yongtao Zhao,Liquan Chen,Xinping Qiu

DOI: https://doi.org/10.1039/b718526j

2008-01-01

Journal of Materials Chemistry

Abstract:The crossover of vanadium ions through proton-exchange membranes such as those of Nafion is the chief reason that results in the low energy efficiency and high self-discharge rate of vanadium redox flow batteries (VRB). With respect to applicability, the ideal proton-exchange membrane used in VRB should possess simultaneously high proton conductivity and low vanadium ion permeability. Here, we report a novel approach using a polyelectrolyte layer-by-layer self-assembly technique to fabricate a barrier layer onto the surface of Nafion membrane by alternate adsorption of polycation poly(diallyldimethylammonium chloride) (PDDA) and polyanion poly(sodium styrene sulfonate) (PSS), which can suppress the crossover of vanadium ions. The Nafion-[PDDA-PSS](n) membrane (n the number of multilayers) obtained shows much lower vanadium ion permeability compared with plain Nafion membrane. Accordingly, the VRB with Nafion-[PDDA-PSS](n) membrane exhibits a higher coulombic efficiency (CE) and energy efficiency (EE) together with a slower self-discharge rate than that of Nafion system. The highest CE of 97.6% and EE of 83.9% can be achieved at charge-discharge current density of 80 mA cm(-2) and 20 mA cm(-2), respectively.
Study on Nafion/Nafion-g-poly (sulfobetaine Methacrylate)-Blended Amphoteric Membranes for Vanadium Redox Flow Battery

Jicui Dai,Hongqiang Zhang,Zhaobin Sui,Huili Hu,Peng Gao,Yongming Zhu,Yichao Dong,Xiangguo Teng

DOI: https://doi.org/10.1007/s11581-019-03228-6

IF: 2.961

2019-01-01

Ionics

Abstract:In order to reduce the vanadium ion permeability while still keep its high stability, atom radical polymerization (ATRP) method was used to introduce zwitterionic sulfobetaine methacrylate (SBMA) onto the Nafion matrix in homogenous solution. The Nafion-grafted poly SBMA (N-g-PSBMA) solution was then used to blend with common Nafion solution to prepare Nafion/Nafion-g-PSBMA (N/N-g-PSBMA) amphoteric membranes by solution casting method. The grafted resins and membranes were characterized by attenuated total reflectance Fourier transform infrared spectra (ATR-FTIR), energy dispersive X-Ray spectroscopy (EDX), scanning electron microscopy (SEM), and water-contact angle analysis. The results prove that the SBMA has been successfully grafted onto the Nafion backbones. Furthermore, the N/N-g-PSBMA membranes have shown higher ion selectivity, coulombic efficiency, and energy efficiency than that of pure recast Nafion (r-Nafion) membrane for VRB application. At the current density of 40–80 mA cm−2, the average energy efficiency of the VRB with N/N-g-PSBMA-20% membrane has reached up to 84.9%, which is 4.2% higher than that of the VRB with the r-Nafion membrane at the same current densities. Moreover, the 100-cycles charge-discharge test proves that the N/N-g-PSBMA-20% membrane possesses higher stability and capacity retention ability than that of r-Nafion membrane, confirming the great potential of such membranes for VRB application.
A Novel Nafion-g-PSBMA Membrane Prepared by Grafting Zwitterionic SBMA Onto Nafion Via SI-ATRP for Vanadium Redox Flow Battery Application

Jicui Dai,Yichao Dong,Cong Yu,Yaxin Liu,Xiangguo Teng

DOI: https://doi.org/10.1016/j.memsci.2018.03.017

IF: 9.5

2018-01-01

Journal of Membrane Science

Abstract:A novel N115-g-PSBMA membrane containing zwitterionic groups was successfully prepared by grafting the zwitterionic SBMA (sulfobetaine methacrylate) onto Nafion 115 (N115) via SI-ATRP (surface-initiated atom transfer radical polymerization) technique. The N115-g-PSBMA membrane has shown higher hydrophilicity, lower vanadium permeability, higher coulombic efficiency and energy efficiency than that of commercial N115 membrane for VRB (vanadium redox flow battery) application. At the current density of 40-80 mA cm(-2), the average energy efficiency of the VRB with N115-g-PSBMA membrane has reached up to 87.3%, which is 2.6% higher than that of the VRB with N115 membrane at the same current densities. The method is expected to present a new direction to prepare novel separators with both excellent performances and low cost for VRB application.
An Advanced Composite Membrane for the All-Vanadium Redox Flow Battery

Maedeh Pahlevaninezhad,Ashutosh Kumar Singh,Thomas Storwick,Elizabeth Esther Miller,Anne Yang,Majid Pahlevani,Michael Pope,Edward P.L. Roberts

DOI: https://doi.org/10.1149/ma2022-013466mtgabs

2022-07-15

ECS Meeting Abstracts

Abstract:Redox flow batteries (RFBs) are a promising technology for grid scale stationary energy storage to complement renewable energy systems. These batteries have a relatively low energy density; however, they offer important advantages, including: long life-time; decoupled energy (arbitrarily large electrolyte volume) and power (electrode area); high round-trip efficiency; scalability and design flexibility; fast response; and low environmental impacts. These advantages make them superior to many energy storage technologies for stationary applications [1-4]. Among the various types of RFBs, vanadium RFBs (VRFBs) are an emerging technology for grid scale energy storage and the integration of renewable energy generation [5]. The membrane is a key component of a VRFB that separates the two half-cell electrolytes and prevents cross-mixing, while allowing the transport of ions during charge-discharge cycles [6]. The VRFB membrane should exhibit low vanadium ion permeability to minimize self-discharge, low cost, and long‐term chemical stability under normal operating conditions. A high proton conductivity and low vanadium ion crossover are known to improve the efficiency of VRFBs [6-7]. In this study, we present a novel composite Nafion based membrane that results in a significant increase in the VRFB performance. The composite membrane has been characterized for its chemical, structural, and thermal properties using appropriate analytical techniques. The battery performance was evaluated in a flow cell using a 'zero-gap' design with an electrode area of 5 cm 2 . The electrolytic solution, 1.6 M VOSO 4 in 3 M H 2 SO 4 , was circulated through the cell. Thermally treated carbon papers were used as the cathode and anode electrodes. For charge-discharge experiments, a constant current density (10 to 80 mA cm −2 ) was applied with upper and lower voltage cut-offs of 1.65 and 0.8 V, respectively. The stability of the battery using the composite membrane was evaluated over 100 cycles. Figures 1 and 2 show the energy efficiency and capacity retention during 100 charge-discharge cycles. The results reveal that the energy efficiency was improved from 51% to 63% by using the composite membrane. In addition, the charge-discharge capacity and capacity retention improved by around 200% and 25%, respectively. This improvement can be attributed to a higher proton conductivity and lower vanadium permeability of the composite membrane. References: [1] M. Skyllas-Kazacos, L. Cao, M. Kazacos, N. Kausar, A. Mousa, Vanadium Electrolyte Studies for the Vanadium Redox Battery-A Review, ChemSusChem. 9 (2016) 1521–1543. [2] A.K. Singh, M. Pahlevaninezhad, N. Yasri, E. Roberts, Degradation of Carbon Electrodes in the All-Vanadium Redox Flow Battery, ChemSusChem. (2021). [3] K.E. Rodby, T.J. Carney, Y. Ashraf Gandomi, J.L. Barton, R.M. Darling, F.R. Brushett, Assessing the levelized cost of vanadium redox flow batteries with capacity fade and rebalancing, J. Power Sources. 460 (2020) 227958. [4] M. Pahlevaninezhad, P. Leung, M. Pahlevani, F. C. Walsh, C. Ponce de Leon, and E. P. L. Roberts, Experimental and Computational Studies of Disperse Blue-1 in Organic Non-Aqueous Redox Flow Batteries, J. Power Sources, Volume 500, 15 July 2021, 229942. [5] X.Z. Yuan, C. Song, A. Platt, N. Zhao, H. Wang, H. Li, K. Fatih, D. Jang, A review of all-vanadium redox flow battery durability: Degradation mechanisms and mitigation strategies, Int. J. Energy Res. (2019). https://doi.org/10.1002/er.4607. [6] X. Li, H. Zhang, Zh. Mai, H. Zhang, I. Vankelecom, Ion exchange membranes for vanadium redox flow battery (VRB) applications, Energy Environ. Sci., 2011, 4, 1147. [7] L. Yu, F. Lin, L. Xua, J. Xi, A recast Nafion/graphene oxide composite membrane for advanced vanadium redox flow batteries, RSC Adv., 2016, 6, 3756. Figure 1
Insights into the Impact of the Nafion Membrane Pretreatment Process on Vanadium Flow Battery Performance.

Bo Jiang,Lihong Yu,Lantao Wu,Di Mu,Le Liu,Jingyu Xi,Xinping Qiu

DOI: https://doi.org/10.1021/acsami.6b03529

IF: 9.5

2016-01-01

ACS Applied Materials & Interfaces

Abstract:Nafion membranes are now the most widely used membranes for long-life vanadium flow batteries (VFBs) because of their extremely high chemical stability. Today, the type of Nafion membrane that should be selected and how to pretreat these Nafion membranes have become critical issues, which directly affects the performance and cost of VFBs. In this work, we chose the Nafion 115 membrane to investigate the effect of the pretreatment process (as received, wet, boiled, and boiled and dried) on the performance of VFBs. The relationship between the nanostructure and transport properties of Nafion 115 membranes is elucidated by wide-angle X-ray diffraction and small-angle X-ray scattering techniques. The self-discharge process, battery efficiencies, electrolyte utilization, and long-term cycling stability of VFBs with differently pretreated Nafion membranes are presented comprehensively. An online monitoring system is used to monitor the electrolyte volume that varies during the long-term charge-discharge test of VFBs. The capacity fading mechanism and electrolyte imbalance of VFBs with these Nafion 115 membranes are also discussed in detail. The optimal pretreatment processes for the benchmark membrane and practical application are synthetically selected.
An Electrolyte with Elevated Average Valence for Suppressing the Capacity Decay of Vanadium Redox Flow Batteries

Zhenyu Wang,Zixiao Guo,Jiayou Ren,Yiju Li,Bin Liu,Xinzhuang Fan,Tianshou Zhao

DOI: https://doi.org/10.1021/acscentsci.2c01112

IF: 18.2

2023-01-31

ACS Central Science

Abstract:Nafion series membranes are widely used in vanadium redox flow batteries (VRFBs). However, the poor ion selectivity of the membranes to vanadium ions, especially for V^(2+), results in a rapid capacity decay during cycling. Although tremendous efforts have been made to improve the membrane's ion selectivity, increasing the ion selectivity without sacrificing the proton conductivity is still a challenging issue. In this work, instead of focusing on enhancing the membranes' ion selectivity, we...

chemistry, multidisciplinary
An Interface-Strengthened Cross-Linked Graphene Oxide/nafion212 Composite Membrane for Vanadium Flow Batteries

Daishuang Zhang,Qian Wang,Sangshan Peng,Xiaoming Yan,Xuemei Wu,Gaohong He

DOI: https://doi.org/10.1016/j.memsci.2019.117189

IF: 9.5

2019-01-01

Journal of Membrane Science

Abstract:An interface-strengthened cross-linked graphene oxide/Nafion212 (CLGO/Nafion212) composite membrane was successfully fabricated and served as ion conducting membrane for vanadium flow batteries (VFBs). Firstly, the surface of Nafion212 was endowed with plenty of amino groups via in situ sol-gel chemistry approach of 3-aminopropyltriethoxysilane. Subsequently, a thin layer of m-xylylenediamino-crosslinked GO was formed using the spin-coating method. The composite membrane demonstrated much lower vanadium ion permeability (0.30x10(-6) cm(2) min(-1)) than pristine Nafion212 (1.88x10(-6) cm(2) min(-1)), mainly due to the presence of a cross-linked GO layer with angstrom-scale channels. The cell assembled with CLGO/Nafion212 exhibited enhanced coulombic efficiencies (CEs, 93.0-97.2% vs. 68.0-91.6%) and energy efficiencies (EEs, 88.9-85.2% vs. 65.7-82.2%) compared with the one with Nafion212 at 20-100 mA cm(-2). At a constant current density of 80 mA cm(-2), the long-term cycling tests showed that the discharge capacity fading of the flow cell equipped with CLGO/Nafion212 reached 0.25% per cycle, which was much smaller than that of Nafion212 (0.47% per cycle). The above findings proved that the cell equipped with CLGO/Nafion212 displayed superior electro-chemical performances than that with Nafion212, therefore CLGO/Nafion212 composite membrane showed a great potential in VFBs.

Rational Use and Reuse of Nafion 212 Membrane in Vanadium Flow Batteries

Nafion/SiO2 Hybrid Membrane for Vanadium Redox Flow Battery

A cost-effective nafion/lignin composite membrane with low vanadium ion permeation for high performance vanadium redox flow battery

A Comparative Study of Nafion Series Membranes for Vanadium Redox Flow Batteries

Performance of a vanadium redox flow battery with a VANADion membrane

Nafion/Organic Silica Hybrid Membrane for Vanadium Redox Flow Battery

A Recast Nafion/graphene Oxide Composite Membrane for Advanced Vanadium Redox Flow Batteries

A high performance polytetrafluoroethene/Nafion composite membrane for vanadium redox flow battery application

Surface-Modified Approach to Fabricate Nafion Membranes Covalently Bonded with Polyhedral Oligosilsesquioxane for Vanadium Redox Flow Batteries

Advanced Nafion hybrid membranes with fast proton transport channels toward high-performance vanadium redox flow battery

Nafion/organically modified silicate hybrids membrane for vanadium redox flow battery

Membrane Development for Vanadium Redox Flow Batteries

Nafion/organic Silica Modified TiO2 Composite Membrane for Vanadium Redox Flow Battery Via in Situ Sol–gel Reactions

Solution casting Nafion/polytetrafluoroethylene membrane for vanadium redox flow battery application

Self-Assembled Polyelectrolyte Multilayer Modified Nafion Membrane with Suppressed Vanadium Ion Crossover for Vanadium Redox Flow Batteries

Study on Nafion/Nafion-g-poly (sulfobetaine Methacrylate)-Blended Amphoteric Membranes for Vanadium Redox Flow Battery

A Novel Nafion-g-PSBMA Membrane Prepared by Grafting Zwitterionic SBMA Onto Nafion Via SI-ATRP for Vanadium Redox Flow Battery Application

An Advanced Composite Membrane for the All-Vanadium Redox Flow Battery

Insights into the Impact of the Nafion Membrane Pretreatment Process on Vanadium Flow Battery Performance.

An Electrolyte with Elevated Average Valence for Suppressing the Capacity Decay of Vanadium Redox Flow Batteries

An Interface-Strengthened Cross-Linked Graphene Oxide/nafion212 Composite Membrane for Vanadium Flow Batteries