Microstructure, Mechanical and Tribological Properties of Oxide Dispersion Strengthened High-Entropy Alloys.

Xinyu Liu,Hangboce Yin,Yi Xu

DOI: https://doi.org/10.3390/ma10111312

IF: 3.4

2017-01-01

Materials

Abstract:A novel metal matrix composite CrMnFeCoNi with Y2O3 as reinforcement phase was designed and manufactured by mechanical alloying and spark plasma sintering. After sintering at 900 °C for 5 min, the microstructure consisted of a FCC matrix and Y2O3 nanoparticles. The addition of 0.25 wt % Y2O3 increased the room temperature tensile strength of the CrMnFeCoNi base from 868 MPa to 1001 MPa, while the mechanical properties of the addition of 0.5 wt % Y2O3 composite decreased. In the meantime, the addition of Y2O3 had no significant influence on the coefficient of friction, while the addition of 0.25 wt % Y2O3 composite shows excellent wear-resistance.