Structure, Intrinsic properties and Vibrational Spectra of Pr(Mg 1/2 Sn 1/2 )O 3 Ceramic Crystal

Hengyang Qiao,Haiqing Sun,Jianzhu Li,Huiling Chen,Chao Xing,Jun Yang,Helei Dong,Jing Wang,Xunqian Yin,Ze-Ming Qi,Feng Shi

DOI: https://doi.org/10.1038/s41598-017-13445-6

IF: 4.6

2017-01-01

Scientific Reports

Abstract:Pr(Mg 1/2 Sn 1/2 )O 3 (PMS) ceramic was prepared through a conventional solid-state reaction method. Crystal structure was investigated through X-ray diffraction (XRD), which certificates that the main phase is PMS with monoclinic P2 1 / n1 symmetry. Lattice vibrational modes were obtained through Raman scattering spectroscopy and Fourier transform far-infrared reflection spectroscopy. The Raman spectrum active modes were assigned and illustrated, respectively, and then fitted with Lorentzian function. The four modes within the range of 110–200 cm −1 are derived from the F 2g vibrations (A-site cations), and the other three modes (300–430 cm −1 ) are derived from the F 2g vibrations (B-site cations).The mode with highest frequency above 650 cm −1 is attributed to A 1g -like mode that corresponds to the symmetric breathing of oxygen octahedral. The far-infrared spectrum with seven infrared active modes was fitted using four-parameter semi-quantum models to calculate intrinsic properties (permittivity and loss). F 2u (2) yielded the greatest contribution to dielectric constant and loss, which is mainly performed as the inverted translational vibration of Pr-MgO 6 octahedron.