Abstract:Nickel-based single crystal superalloys, as engine blade materials, are prone to fatigue damage due to repeated startups and shutdowns. Therefore, monitoring and quantitatively estimating fatigue cracks are essential for engineering structures to ensure safety. In this study, we proposed a method for fatigue crack segmentation and damage prediction based on deep learning and in-situ high-temperature scanning electron microscopy (SEM). Sequential SEM images describing the crack initiation and propagation under near-service conditions were obtained by conducting in-situ high-temperature fatigue experiments. A fatigue crack dataset with high-quality was thus constructed for further dynamic and real-time crack segmentation and damage assessment. Deep learning-based models were used to segment cracks and predict damage behavior (i.e., crack area, length, width, and stress intensity factors) at future based on prior damage information. The short-term and long-term damage prediction capability were validated by comparing model performance when predicting damage at different future time points. Additionally, we compared the model performance when predicting damage at specific time point based on varying lengths of input sequence. Results demonstrated that the model could segment cracks and scales with different sizes accurately. The model performed well in short-term damage prediction. The long-term predictive performance showed decrease than that of short-term, which could be improved by feeding long length of input sequence. The proposed approach demonstrates the feasibility and effectiveness of deep learning-based crack segmentation and damage prediction, which facilitates the move toward real-time analysis and rapid diagnosis of material damage in the future.

On the Use of Data-Driven Machine Learning for Probabilistic Fatigue Life Prediction of Metallic Materials Based on Mesoscopic Defect Analysis

Fatigue life prediction driven by mesoscopic defect data

Fatigue life prediction of aluminum alloy 6061 based on defects analysis

Physics-guided Machine Learning Frameworks for Fatigue Life Prediction of AM Materials

A Process-Data-driven BP Neural Network Model for Predicting Interval-Valued Fatigue Life of Metals

Continuum Damage Mechanics Based Probabilistic Fatigue Life Prediction for Metallic Material

Multiaxial Fatigue Life Prediction Based on Damage Mechanics and Critical Plane Method

Prediction of Fatigue Crack Damage Using In-Situ Scanning Electron Microscopy and Machine Learning

Machine learning-based fatigue life prediction of metal materials: Perspectives of physics-informed and data-driven hybrid methods

Critical physics informed fatigue life prediction of laser 3D printed AlSi10Mg alloys with mass internal defects

The potency of defects on fatigue of additively manufactured metals

A machine-learning fatigue life prediction approach of additively manufactured metals

A new data-driven probabilistic fatigue life prediction framework informed by experiments and multiscale simulation

Machine learning based very-high-cycle fatigue life prediction of AlSi10Mg alloy fabricated by selective laser melting

Fatigue Life Prediction of Cold Expansion Hole Using Physics-Enhanced Data-Driven Method

Probabilistic Life Prediction for High Temperature Low Cycle Fatigue Using Energy-Based Damage Parameter and Accounting for Model Uncertainty

A physics‐informed neural network framework based on fatigue indicator parameters for very high cycle fatigue life prediction of an additively manufactured titanium alloy

Probabilistic Method to Predict Fatigue Life Based on Crack Initiating Micro-Mechanism of Aluminum Alloy

Machine learning assisted probabilistic creep-fatigue damage assessment

On the use of data-driven machine learning for remaining life estimation of metallic materials based on Ye-Wang damage theory

A Probabilistic Model for Prediction of Life Based on Probabilistic Character of Defects in PM Alloys