Abstract:The catalytic conversion of syngas to higher alcohols (C 2+ OH) has drawn widespread attention because it can alleviate the oil crisis and realize the clean and efficient use of coal. Nevertheless, the seesaw problem between C 2+ OH and total alcohol selectivity has not been solved. In recent years, catalytic processes involving oxygen vacancies have been widely investigated. However, the existing literature on this topic is fragmentary and unsystematic. Herein, we report a significant improvement in C 2+ OH synthesis by varying the oxygen vacancies on CuZn catalysts and systematically elaborate the structural and catalytic effects of the oxygen vacancies. Oxygen vacancy content shows almost linear positive correlations with many of the physical and chemical properties of the catalysts, such as S BET , V p , D p , Cu 0 size, H 2 consumption, and Cu 0 /(Cu 0 + Cu + ) ratio. The presence of oxygen vacancies drives catalysis in two ways. One, the dissociation of water adsorbed on oxygen vacancies causes the formation of hydroxyl groups, which interact with activated CO* to form surface formate (HCOO*) groups. This is followed by successive hydrogenation to form surface CH x O* intermediates. The CH x O* or CO* species are then coupled with surface CH x * to form ethanol on Zn δ+ defect sites, realizing the growth of carbon chains. Two, oxygen vacancies drive electron transfer from ZnO to Cu, generating more Zn δ+ defects and regulating the Cu 0 /(Cu 0 + Cu + ) ratio. The presence of electron-rich Cu is conducive to CO dissociation and adsorption, which promotes the formation of the critical surface intermediate CH x *. Consequently, the optimized CZ-0.80 catalyst exhibits exceptional catalytic performance, achieving 9.98 % CO conversion as well as ethanol and C 2+ OH proportions of up to 54.27 % and 59.95 %, respectively. Thus, by developing a new catalyst system that avoids the use of F-T elements such as Co or Fe for C 2+ OH synthesis from syngas, this work provides a new understanding of the growth of carbon chains.

Oxygen vacancies boosted Co-Co2C catalysts for higher alcohols synthesis from syngas

Investigation of the role of oxygen vacancies in CuZn catalysts for the formation of higher alcohols from syngas

Cerium doped Co/AC catalysts for higher alcohols synthesis from syngas

Constructing the active pairs of Co0-Co2+ via surface solid reaction on TiO2 with the additives of La and Al for higher alcohols synthesis

Synthesis of tetrahedrally coordinated CoO for higher alcohol synthesis directly from syngas

Theoretical investigation of the selectivity of alcohols and aldehydes on Co-based catalysts in syngas conversion

Co–Co2C catalysts supported on carbon-coated ordered mesoporous silica with promoted CO insertion and C–C coupling for higher alcohol synthesis from syngas

Regulating Oxygen Vacancies for Enhanced Higher Oxygenate Synthesis via Syngas

Optimizing surface oxygen vacancy sites for CO hydrogenation to isobutanol over ZnCr catalyst

Oxygen Vacancy Engineering Through Equivalent and Aliovalent Doping on Lacoo3

The bifunctional oxygen carrier K/LayCoxFe1-xO3 for the production of C2–C4 olefins via CO2 hydrogenation

Ultrathin and Vacancy-Rich CoAl-Layered Double Hydroxide/Graphite Oxide Catalysts: Promotional Effect of Cobalt Vacancies and Oxygen Vacancies in Alcohol Oxidation

Synthesis of higher alcohols by CO hydrogenation over catalysts derived from LaCo1-xMnxO3 perovskites: Effect of the partial substitution of Co by Mn

Oxygen Vacancy Control of Catalytic Activity of Cu/ZnO for Higher Alcohols Synthesis via Incorporating Ga

Effects of alkali promoters on tri-metallic Co-Ni-Cu-based perovskite catalyst for higher alcohol synthesis from syngas

Oxygen vacancy promoted carbon dioxide activation over Cu/ZrO2 for CO2-to-methanol conversion.

Promoting effect of oxygen vacancies in Co/CoAl 2 O 4 catalyst steered with a straightforward method on hydrogenation of furfural to 2-methylfuran

Alcohol Synthesis via Fischer–Tropsch Synthesis over Activated Carbon Supported Alkaline Earth Modified Cobalt Catalyst

High Alcohols Synthesis via Fischer–Tropsch Reaction at Cobalt Metal/Carbide Interface

Graphene oxide-ordered mesoporous silica composite supported Co-based catalysts for CO hydrogenation to higher alcohols

Higher alcohols synthesis from syngas over P-promoted non-noble metal Cu-based catalyst