Abstract:The integration of nickel (Ni) nanoparticle (NP)-embedded carbon layers (Ni@C) into the three-dimensional (3D) hierarchically porous carbon architectures, where ultrahigh boron (B) and nitrogen (N) doping is a potential methodology for boosting Ni catalysts' water splitting performances, was achieved. In this study, the novel 3D ultrafine Ni NP-embedded and B- and N-codoped hierarchically porous carbon nanowires (denoted as Ni@BNPCFs) were successfully synthesized via pyrolysis of the corresponding 3D nickel acetate [Ni(AC)2·4H2O]-hydroxybenzeneboronic acid-polyvinylpyrrolidone precursor networks woven by electrospinning. After optimizing the pyrolysis temperatures, various structural and morphological characterization analyses indicate that the optimal Ni@BNPCFs-900 networks own a large surface area, abundant micro/mesopores, and vast carbon edges/defects, which boost doping a large amount of B (5.81 atom %) and N (5.84 atom %) dopants into carbon frameworks with 6.36 atom % of BC3, pyridinic-N (pyridinic-N-Ni), and graphitic-N active sites. Electrochemical measurements demonstrate that Ni@BNPCFs-900 reveals the best hydrogen evolution reaction (HER) and oxygen reduction reaction catalytic activities in an alkaline solution. The HER potential at 10 mA cm-2 [E10 = -164.2 mV vs reversible hydrogen electrode (RHE)] of the optimal Ni@BNPCFs-900 is just 96.2 mV more negative than that of the state-of-the-art 20 wt % Pt/C (E10 = -68 mV vs RHE). In particular, the OER E10 and Tafel slope of the optimal Ni@BNPCFs-900 (1.517 V vs RHE and 19.31 mV dec-1) are much smaller than those of RuO2 (1.557 V vs RHE and 64.03 mV dec-1). For full water splitting, the catalytic current density achieves 10 mA cm-2 at a low cell voltage of 1.584 V for the (-) Ni@BNPCFs-900||Ni@BNPCFs-900 (+) electrolysis cell, which is 10 mV smaller than that of the (-) 20 wt % Pt/C||RuO2 (+) benchmark (1.594 V) under the same conditions. The synergistic effects of 3D hierarchically porous structures, advanced charge transport ability, and abundant active centers [such as Ni@BNC, BC3, pyridinic-N (pyridinic-N-Ni), and graphitic-N] are responsible for the excellent water-splitting catalytic activity of the Ni@BNPCFs-900 networks. Especially, because of the remarkable structural and chemical stabilities of 3D hierarchically porous Ni@BNPCFs-900 networks, the (-) Ni@BNPCFs-900||Ni@BNPCFs-900 (+) water electrolysis cell displays an excellent stability.

Ni and CeO 2 Nanoparticles Anchored on Cicada-Wing-like Nitrogen-Doped Porous Carbon as Bifunctional Catalysts for Water Splitting

Cerium-Doped Nickel Sulfide Nanospheres as Efficient Catalysts for Overall Water Splitting

Ni3N–CeO2 Heterostructure Bifunctional Catalysts for Electrochemical Water Splitting

Facile generation of CeO 2 nanoparticles on multiphased NiS x nanoplatelet arrays as a free-standing electrode for efficient overall water splitting

CeO 2 -decorated Fe-doped Ni 2 P nanosheets for efficient electrocatalytic overall water splitting at high current densities

Electronically Modulated Nickel Boron by CeOx Doping As a Highly Efficient Electrocatalyst Towards Overall Water Splitting.

Electronic Regulation of Ce,F-Ni2P/CoP Catalyst for Efficient Water Splitting

Facile Construction of Heterostructural Ni3(NO3)2(OH)4/CeO2 Bifunctional Catalysts for Boosted Overall Water Splitting

Quantum dot-doped CeOx–NiB with modulated electron density as a highly efficient bifunctional electrocatalyst for water splitting

Anchoring Ni2P Sheets on NiCo2O4 Nanocone Arrays as Optimized Bifunctional Electrocatalyst for Water Splitting

Nested-Like Cerium-Doped Cop Nanowires As an Efficient and Durable Electrocatalyst for Overall Water Splitting in Alkaline Medium

Partially Oxidized Ni Nanoparticles Supported on Ni-N Co-Doped Carbon Nanofibers As Bifunctional Electrocatalysts for Overall Water Splitting

Ni2P(O)–Fe2P(O)/CeOx as high effective bifunctional catalyst for overall water splitting

Synergistic Coupling of Ni Nanoparticles with Ni3 C Nanosheets for Highly Efficient Overall Water Splitting

Highly Active and Durable Nitrogen-Doped Cop/Ceo2 Nanowire Heterostructures for Overall Water Splitting

Electronic modulation of sprout-shaped NiCoP nanoarrays by N and Ce doping for efficient overall water splitting

In Situ Constructing Lamella-Heterostructured Nanoporous CoFe/CoFe2O4 and CeO2−x As Bifunctional Electrocatalyst for High-Current-density Water Splitting

Electronically modulated nickel boron by CeO x doping as a highly efficient electrocatalyst towards overall water splitting

Tiny Ni Nanoparticles Embedded in Boron- and Nitrogen-Codoped Porous Carbon Nanowires for High-Efficiency Water Splitting

Synergistically Coupled Ni/CeOx@C Electrocatalysts for the Hydrogen Evolution Reaction: Remarkable Performance to Pt/C at High Current Density

Confined synthesis of highly dispersed Ni anchored on mesoporous carbon as efficient catalyst for water splitting