Influences of Cooling Rate on Solidification Microstructure and Carbide of GCr15 Bearing Steel
Luo, Tengfei
DOI: https://doi.org/10.1007/s11663-023-02725-4
2023-02-16
Metallurgical Transactions B (Process Metallurgy)
Abstract:For improving the quality and performance of bearings, it is necessary to investigate the precipitation mechanism of carbides in the solidification of GCr15 steel under conditions of continuous casting. Thus, the present work took the continuously cast GCr15 steel with the transverse section of 240 mm × 240 mm in a domestic steel plant as the research object. First, a two-dimensional solidification heat transfer model was developed and verified with the temperature measured via the infrared thermal imager. So, the average cooling rate in the mushy zone at 20, 40, 60, 80, 100, and 120 mm below the inner surface of the billet were determined. Second, the solidification of GCr15 steel at these locations under the corresponding continuous casting condition was simulated via a high-temperature confocal scanning laser microscope (HT-CSLM). Third, the effects of cooling rates on the characteristics of the solidification microstructure and carbides were analyzed. The results show that at 20, 40, 60, 80, 100, and 120 mm below the inner surface, the average cooling rates in the mushy zone are 57.28, 24.70, 18.44, 17.02, 17.54, and 18.95 K/min, the average equivalent diameters of the carbides are 7.93, 8.64, 10.50, 11.40, 11.21, and 9.99 μ m, respectively. The carbides usually precipitate together with phosphides and grow in the inter-dendritic region which is the last area to solidify. Besides the homogeneous nucleation, carbides sometimes nucleate on Al 2 O 3 -MnS or MnS inclusions. Carbides are irregular polygons usually with sharp corners and arc edges. The atom ratio between metal and non-metallic elements is within 3.33 to 4.89. Dot-like segregation and uniform segregation of P are observed in the carbides at the cooling rate of 57.28 and 17.02 K/min. However, the segregation characteristics of C and Cr change little with the cooling rate. The geometric mean of primary and secondary dendrite arm spacings ( , μ m) decreases with the increase of the cooling rate ( R c , K/min), and their functional relationship is . Because of the decrease of the size of the solidification structure, the carbides become overall smaller with the increase in the cooling rate. According to the micro-segregation calculation, solutes of C, Cr, and P elements gradually enrich in the liquid phase, especially P at the end of solidification. The cooling rate influences not only the time for the back diffusion, but also the size of the local solidification region. Under the premise of the present work, the segregation ratio of the interstitial element C increases slightly with the decrease of the cooling rate. However, for Cr and P with the limited diffusivity, the segregation ratio first decreases as the cooling rate declines from 57.28 to 24.70 K/min, and then increases closely to that at 57.28 K/min as the cooling rate decreases to 17.02 K/min. Compared with C and Cr, P is influenced more by the cooling rate. So, the segregation characteristics of C, Cr, and P in the carbide are qualitatively interpreted.