Abstract:To improve the mechanical properties of the surface of iron-based alloys, a ZrC–Fe coating is produced on cast ion via in situ solid-phase diffusion (ISSD) at 1130 °C. The coating is completely dense, reaching a thickness of approximately 18 μm after 10 h of ISSD. The volume fraction of the ZrC phase in the coating reaches approximately 92.3%. The size of the long axis (short axis) of columnar ZrC particles gradually decreases from approximately 4 μm (1.5 μm) to 1 μm (0.3 μm) as the thickness of the coating increases, displaying a gradient microstructure. The formation mechanism of the coating is mainly attributed to the carbon atoms diffuse into the octahedral vacancies of the zirconium lattice to undergo a diffusion-type solid state phase transformation to form ZrC, and α-Fe phase are distributed among the ZrC particles through the Fe atoms diffusion. Due to the carbon concentration gradient, the nucleation rate is reduced, thereby forming a gradient microstructure on the grain scale. The growth of the coating obeys the growth kinetic model d2=30.5t. In addition, the nanohardness and elastic modulus of the surface of the ZrC–Fe coating reach 29.7 GPa and 425.1 GPa, respectively, showing remarkable improvement compared to those of the cast iron substrate (4.5 GPa and 229.5 GPa, respectively). The fracture toughness gradually increases from 2.9 ± 0.1 MPa m1/2 to 3.6 ± 0.1 MPa m1/2 as the thickness of the coating increases. Moreover, the coating exhibits the superior coating/substrate adhesion. The excellent comprehensive mechanical properties are tightly related to a small amount of high toughness α-Fe phase, high volume fraction of in situ ZrC particles and the gradient change of the ZrC grain scale.

Mechanical Properties of Vermicular Graphite Cast Iron Processed by Selective Laser Surface Alloying with Ultra-fine ZrO 2 Ceramic Particulates

Mechanical Properties and Wear Resistance of ZrO2 Particulate-Reinforced Composite Layer on Compacted Graphite Cast Iron Processed by Selective Laser Alloying

Mechanical Properties of Composite Coating on Cast Iron by Laser

Fabrication of Nanocrystalline Zro2 Particle Reinforced Aluminum Alloy Composite by Squeeze Casting Route

Microstructure and wear characteristics of ATZ ceramic particle reinforced gray iron matrix surface composites

The Fabrication and Properties of Particle Reinforced Cast Metal Matrix Composites

Microstructure, Formation Mechanism and Mechanical Properties of ZrC–Fe Coating on Cast Iron Via in Situ Solid-Phase Diffusion

TiC Reinforcement Composite Coating Produced Using Graphite of the Cast Iron by Laser Cladding

Interfacial Bonding And Abrasive Wear Behavior Of Iron Matrix Composite Reinforced By Ceramic Particles

Influences of Dual-Phased Nanoparticles on Microstructure, Mechanical Properties and Wear Resistance of Vermicular Graphite Cast Iron

Mechanism of Zr in in situ-synthesized particle reinforced composite coatings by laser cladding

Elucidation of Abrasive Wear and Slurry Erosion Behavior of Fe Matrix Composites Reinforced with Metallic Coating Modified ZTAP Ceramics

On the Preparation and Wear Properties of Ceramic Particle-reinforced High-chromium Cast Iron-based Surface Composite Material

Three-body Abrasive Wear Resistance of Iron Matrix Composites Reinforced with Ceramic Particles

Wear Resistance Of Austenite-Tic-Graphite Microstructures Prepared By Laser Coating

Research on Laser Cladding Co-Based Alloy on the Surface of Vermicular Graphite Cast Iron

Microstructural Properties of Particle-Reinforced Multilayer Systems of 316L and 430L Alloys on Gray Cast Iron

Interfacial Bonding and Abrasive Wear Behaviours of the Iron Matrix Composites

Effects of Graphite Addition on the Microstructure and Properties of Laser Cladding Zr–Al–Ni–Cu Amorphous Coatings

Preparation and Properties of ZTA + WC Particles/Hypereutectic High Chromium Cast Iron Composites

The Microstructures and Tribological Properties of Composite Coatings Formed Via PTA Surface Alloying of Copper on Nodular Cast Iron