Controllable synthesis and characterization of Fe3O4/Au composite nanoparticles
yan xing,yanyan jin,jianchao si,mingli peng,xiaofang wang,chao chen,yali cui
DOI: https://doi.org/10.1016/j.jmmm.2014.09.060
IF: 3.097
2015-01-01
Journal of Magnetism and Magnetic Materials
Abstract:Fe3O4/Au composite nanoparticles (GoldMag NPs) have received considerable attention because of their advantageous properties arisen from both individual Au and Fe3O4 nanoparticles. Many efforts have been devoted to the synthesis of these composite nanoparticles. Herein, GoldMag NPs were reported to be synthesized by two-step method. Fe3O4 nanoparticles were prepared by co-precipitation and modified by the citric acid, and then citric acid-coated Fe3O4 nanoparticles were used as seeds in sodium citrate solution to reduce the HAuCl4. The size of obtained nanoparticles was geared from 25 to 300nm by controlling the concentration of reactants. The GoldMag NPs were characterized by UV–vis spectrometer, dynamic light scattering (DLS), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and vibrating sample magnetometer (VSM). The GoldMag NPs showed good superparamagnetism at room temperature and were well dispersed in water with surface plasmon resonance absorption peak varied from 538nm to 570nm.