First-principle calculation and assignment for vibrational spectra of Ba (Mg 1/2 W 1/2) O 3 microwave dielectric ceramic
Chuanling Diao,Chunhai Wang,Nengneng Luo,ZeMing Qi,Tao Shao,Yuyin Wang,Jing Lu,Feng Shi,Xiping Jing
DOI: https://doi.org/10.1111/jace.12429
IF: 4.186
2013-01-01
Journal of the American Ceramic Society
Abstract:Ba(Mg1/2W1/2)O3 ceramic was synthesized using a conventional solid-state reaction method at 1500 degrees C for 4h. The face-centered cubic crystal structure of the material was confirmed by Rietveld refinement of X-ray diffraction (XRD) data, and vibrational modes were obtained by Raman and Fourier transform far-infrared (FTIR) reflection spectroscopies. First-principle calculations based on density functional theory with local density approximation were used to calculate Gamma-point modes and dielectric properties of Ba(Mg1/2W1/2)O3. The Raman spectrum with nine active modes can be fitted with Lorentzian function, and the modes were assigned as F2g(1) (126cm-1), F2g(2) (441cm-1), Eg(O) (538cm-1), and A1g(O) (812cm-1). Far-infrared spectrum with 12 infrared active modes was fitted using both the Lorenz three-parameter classical and four-parameter semiquantum models. Consequently, the modes were assigned as F1u(1) (144cm-1), F1u(2) (284cm-1), F1u(3) (330-468cm-1), and F1u(4) (593-678cm-1). The active modes were represented by linear combinations of symmetry coordinates that were obtained by group theory analyses. The Raman mode A1g, which has the highest wave number (812cm-1) is dominated by the breath vibration of the MgO6 octahedron. The infrared modes F1u(2), that can be described as the inverted vibrations of Mg atoms in the MgO6 octahedron along the xi, yi, and zi axes have the most contributions to the microwave permittivity and dielectric loss.