Abstract:In this study, heat-treated and multisurface engineered DIN 1.2367 tool steel was subjected to room and elevated temperature wear tests, and the effect of nitriding on its tribological behavior was investigated. CrN, AlTiN, and CrN/AlTiN coatings with a total thickness of 2 μm were obtained by arc cathodic physical vapor deposition on conventional heat-treated and gas-nitrided steels. The white layer formed during nitriding was removed, and a diffusion layer (100 μm) was achieved in the cross section of the steel having a tempered martensitic matrix. The highest surface hardness was attained with an integral coating (CrN/AlTiN), and surface hardness increased even more after nitriding due to the formation of a multicomponent ceramic layer on top of the diffusion layer. The room temperature wear tests performed against an alumina counterpart revealed that (i) CrN/AlTiN-coated steel had the highest friction coefficient of 0.26, which further increased to 0.33 by nitriding due to the increase in shear strength, and that (ii) with increasing surface hardness, the specific wear rates (W) of the heat-treated and coated steels could be ranked as follows: WCrN/AlTiN < WAlTiN < WCrN. The wear rates decreased when nitriding was carried out prior to coating. In order to simulate the aluminum extrusion conditions, hot wear behavior of the surfaces against AA6080 alloy at 450 °C was investigated. The hot wear tests revealed that (i) high friction coefficients were reached due to the adhesive characteristic of aluminum to the surfaces, (ii) the nitrided and CrN/AlTiN-coated sample exhibited the lowest wear rate among all studied surfaces, and (iii) the film damage on the worn surfaces mostly occurred in the form of droplet delamination.

A Novel Single-Step Surface-Treatment Process for Forming Cr-Nitride Coatings on Steels

Formation of Chromium Nitride Coatings on Carbon Steels by Pack Cementation Process

Improved Nitrogen Transport in Surface Nanocrystallized Low-Carbon Steels During Gaseous Nitridation

Formation of nanostructured Cr2N/CrN layer on plain 20 carbon steelby duplex chromizing process

Formation of Nanostructured Cr2N/CrN Layer on Plain 20 Carbon Steel by Duplex Chromizing Process

Formation of hard surface layer on austenitic stainless steels via simultaneous chromising and nitriding by pack cementation process

Microstructure Characteristics and Formation Mechanism of Co-Deposition Coating on Plain 45# Carbon Steel via Simultaneous Chro-mising and Nitriding by Pack Cementation Process

Microstructure, Adhesion and Tribological Properties of CrN/CrTiAlSiN/WCrTiAlN Multilayer Coatings Deposited on Nitrocarburized AISI 4140 Steel

Gaseous Nitriding Process of Surface Nano Crystallized (snced) Steel

Formation of A Nanostructured Crn Layer on Nitrided Tool Steel by Low-Temperature Chromizing

Increasing surface hardness of austenitic stainless steels by pack nitriding process

Microstructure, Mechanical and Adhesive Properties of CrN/CrTiAlSiN/WCrTiAlN Multilayer Coatings Deposited on Nitrided AISI 4140 Steel

Formation Kinetics and Properties of CrNx/H13 Functionally Graded Coating Fabricated by PVD

Theoretical Calculations and Experimental Study of the Nitrided Layer of 1Cr17Ni2 Steel

Phase transformations in low-temperature chromized 0.45 wt.% C plain carbon steel

Preparation and electrochemical properties of gradient CrNx coatings on H13 steel

Surface Modification of Chromium–Nickel Steel by Electrolytic Plasma Nitriding Method

Effect of Plasma Nitriding Pretreatment on the Mechanical Properties of AlCrSiN-Coated Tool Steels

Microstructure evolution and mechanical performance of Cr-N/Al-Cr multilayer coatings produced by plasma nitriding Cr-coated Al alloy

Synthesis of Corrosion-Resistant Coatings by Non–Vacuum Electron Beam Surfacing: Production, Structure, and Properties

Nitriding Effect on the Tribological Performance of CrN-, AlTiN-, and CrN/AlTiN-Coated DIN 1.2367 Hot Work Tool Steel