Abstract:The fabrication of superhydrophobic coatings on mild steel has attracted considerable attention. However, some methods are cumbersome and unsuitable for large-scale preparation, limiting industrial applications. Furthermore, the extensive use of fluorinated compounds to achieve low surface energy is not environmentally friendly. This paper proposed a facile method based on electrodeposition and annealing to prepare mild steel-based superhydrophobic surfaces without chemical modifications. Subsequently, SEM images were analyzed, and it was observed that the plating parameter (current and time) significantly affected surface morphology. At optimum process parameters, a rough surface with a multi-level structure was formed on the plated surface, contributing to superhydrophobic properties. XPS, EDS, and XRD were utilized to analyze surface composition. The results indicated the presence of copper oxides, zinc oxides, and a large number of hydrocarbons on the prepared superhydrophobic surface. These transition metal oxides on the surface adsorbed hydrocarbons in the air during the annealing process, which lowered the surface energy. Combined with the obtained multi-level morphology, a superhydrophobic surface was achieved. Finally, the corrosion behavior was evaluated in 3.5 wt% NaCl solution by AC impedance spectroscopy. Results showed that the obtained superhydrophobic surface, compared with the untreated coating and the steel substrate, showed a substantial improvement in corrosion resistance. A mild steel-based superhydrophobic surface with a contact angle greater than 150 degrees and excellent corrosion resistance was finally obtained. We hope this study will facilitate the industrial preparation of superhydrophobic coatings, especially in marine engineering, since this method does not require complex processes or expensive equipment and does not require fluorinated substances.

Facile Preparation of Superamphiphobic Phosphate–cu Coating on Iron Substrate with Mechanical Stability, Anti-Frosting Properties, and Corrosion Resistance

Fast and Low-Cost Method to Fabricate Large-Area Superhydrophobic Surface on Steel Substrate with Anticorrosion and Anti-Icing Properties

Facile Fabrication of Iron-Based Superhydrophobic Surfaces Via Electric Corrosion Without Bath

Preparation of Robust CuO/TiO2 Superamphiphobic Steel Surface through Chemical Deposition and Sol–Gel Methods†

Facile and Eco-Friendly Preparation of Mild Steel Based Superhydrophobic Surfaces without Chemical Modifications

Facile Fabrication of Superhydrophobic Surface with Excellent Mechanical Abrasion and Corrosion Resistance on Copper Substrate by a Novel Method.

Hybrid superamphiphobic anti-corrosion coating with integrated functionalities of liquid repellency, self-cleaning, and anti-icing

Preparation of superhydrophobic nanoplate iron oxide surface on a carbon steel for anti-wetting applications

Superhydrophobic coating on heat-resistant steel surface fabricated by a facile method

A Facile and Gentle Method to Fabricate NH4CoPO4 Coating with Superhydrophobic Character Study

Heat Treatment of PTFE/PDMS/Nano‐silica Deposited Layer for Preparation of Superhydrophobic Coating with Anti‐corrosion, Anti‐scaling, and Anti‐fouling Properties

Facile preparation of a robust superhydrophobic SiO2/epoxy composite coating with favorable corrosion and scale inhibition performance

Preparation of a Superamphiphobic Surface on a Common Cast Iron Substrate

The Preparation and Properties of a Ni-SiO2 Superamphiphobic Coating Obtained by Electrodeposition

Facile Fabrication of Biomimetic Superhydrophobic Surface with Anti-Frosting on Stainless Steel Substrate

Spray-coated Superhydrophobic Surfaces with Wear-Resistance, Drag-Reduction and Anti-Corrosion Properties

A Novel Method to Fabricate Water-Soluble Hydrophobic Agent and Super-Hydrophobic Film on Pretreated Metals

Superhydrophobic and Superoleophobic Surface by Electrodeposition on Magnesium Alloy Substrate: Wettability and Corrosion Inhibition

Rose-like Cr–Fe robust super-hydrophobic surfaces with high adhesion and corrosion resistance

Facile Fabrication of Super-Hydrophobic Surfaces by Spray PTFE

Controllable fabrication of stable superhydrophobic surfaces on iron substrates