Promoting form I' Crystallization and Melting-recrystallization By Adding a β-Nucleating agent into Poly(butene-1)/isotactic Polypropylene Blends
Min Xu,Yu Han,Xiangyang Li,Jianjun Ding,Kang Zheng,Yongxing Lin,Lin Chen,Xing-You Tian
DOI: https://doi.org/10.1039/d3ce00212h
IF: 3.756
2023-03-31
CrystEngComm
Abstract:As the main factor restricting the production of poly(1-butene), the slow phase transition of poly(1-butene) from form II to form I has not been avoided effectively because of lacking effective methods. Blending with other polyolefins to directly transit into stable form I' crystal could be a possible solution, however, such a method hardly inhibits the formation of form II completely. What is worse, the obtained form I' crystal even has a lower thermostability than that of form II, which makes it hard to be an ideal solution. In this study, employing FTIR, XRD, SEM and POM, we found that adding a moderate amount of WBG-II, a nucleating agent of iPP, into isotactic polypropylene/poly(1-butene) (iPP/PB-1) blends could promote the formation of form I' greatly. More importantly, the melted form I' can rapidly recrystallize into form II on heating, improving thermostability. The lower the quenching temperature, the more significant the role of WBG-II. We conjectured that the effect of WBG-II could be related to iPP chains in the PB-rich domains, because the promotion effect of WBG-II only becomes significant when PB-1 content is greater than 20% but smaller than 80%, where PB-rich domains may exist. The addition of WBG-II enhanced nucleating ability of iPP chains in the PB-rich domains and therefore increased its ability to promote form I' nucleation. After increasing temperature above the melting point of form I', the iPP nuclei formed under the assistance of WBG-II in turn act as nucleation sites of form II, promoting form I' transiting into form II after melting. This study provides a new idea to avoid the influence of slow form II to form I phase transition on the production of PB-1 and improve the thermostability of PB-1.
chemistry, multidisciplinary,crystallography