Ultrasmall Noble Metal Doped Ru 2 P@Ru/CNT as High-Performance Hydrogen Evolution Catalysts
Hongfu Miao,Dan Zhang,Yue Shi,Xueke Wu,Wen Zhang,Xilei Chen,Jianping Lai,Lei Wang
DOI: https://doi.org/10.1021/acssuschemeng.1c06222
2021-10-29
Abstract:At present, the development of hydrogen evolution reaction (HER) catalysts with intrinsic activity higher than that of Pt/C still faces great challenges. In this work, we synthesized a series of ultrasmall (<5 nm) surfactant-free M–Ru2P@Ru/CNTs (M = Pt, Pd, Rh, and Ir; CNTs = carbon nanotubes) via a solvent-free microwave method in a household microwave oven within 1 min for the first time. Electronic and chemical effects caused by heterojunction and doping in M–Ru2P@Ru/CNTs can effectively promote HER. After optimizing the components and proportions, Pt–Ru2P@Ru/CNT with a Pt content of 9.5% (Pt0.095–Ru2P@Ru/CNT) exhibits the highest catalytic properties, with low overpotentials of 14 and 27 mV in 1 M KOH and 0.5 M H2SO4, respectively, outperforming most reported Ru-based catalysts. Moreover, the electrochemically active surface area (ECSA) of the Pt0.095–Ru2P@Ru/CNT can reach 165 m2/g. Also, turnover frequency (TOF) values under alkaline and acidic conditions are 21 and 54 s–1, respectively. The high current activity of the Pt0.095–Ru2P@Ru/CNT was also explored. Achieving current densities of 1000 mA cm–2 in alkaline and acidic electrolytes requires only 109 and 135 mV, respectively. Furthermore, the strong interaction between ultrasmall nanoparticles and CNTs can make nanoparticles firmly anchored on CNTs. After 120 h of stability testing under various conditions, they still retain excellent activity.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology