Abstract:Because of the favorable mass transport and increased available active sites, the rational design and preparation of porous carbon structures are essential but still challenging. Herein, a novel and facile supramolecular anchoring strategy was developed to achieve the embedding of ruthenium (Ru) nanoparticles in N-doped mesoporous carbon nanospheres through pyrolyzing the precursor formed by coordination assembly between metal ions and zinc gluconate (G(Zn)). Featuring rich hydroxyl groups, the G(Zn) can effectively chelate Ru3+ via metal-oxygen bonds to form 3D supramolecular nanospheres, and meanwhile, mesopores in carbon nanospheres were expanded after subsequent pyrolysis thanks to the volatilization of zincic species at high temperature. As a demonstration, the best-performing catalyst displayed extraordinary activity for the hydrogen evolution reaction (HER) with a small overpotential of 43 mV versus reversible hydrogen electrode (vs RHE) at 10 mA/cm2 and a Tafel slope of 39 mV/dec, which was superior to that of commercial Pt/C in alkaline medium. Theoretical calculations revealed that the catalytic activity was significantly promoted by the strong electronic coupling between Ru nanoparticles and N-doped porous carbon, which increased the electron transfer capability and facilitated the adsorption and dissociation of H2O to realize an efficient HER.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c07435?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c07435</a>.Supplementary Figures S1–S16: The SEM and HRTEM images and N2 adsorption–desorption isotherm of G-Ru(100:1); the SEM and HRTEM images, XRD, XPS, and N2 adsorption–desorption isotherm of G-Ru(200:1) and G-Ru(50:1), respectively; the XPS spectra of commercial Pt/C; the comparison of HER performance of G(Zn)-Ru(100:1) that underwent pyrolysis with different atmospheres; the EIS plots of various catalysts and the corresponding circuit diagram; the Cu UPD curves of various catalysts; the calculated mass activity of various catalysts; the characterization of G(Zn)-Ru(100:1) after the stability test; the site-dependent PDOSs of Ru-4d in Ru-diamond and Ru-graphene; and a summary of catalytic activity of Ru-based and transition metal-based electrocatalysts (Table S1) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c07435/suppl_file/am1c07435_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Controllable fabrication of uniform ruthenium phosphide nanocrystals for the hydrogen evolution reaction

Facile Synthesis of Pd@Ru Nanoplates with Controlled Thickness As Efficient Catalysts for Hydrogen Evolution Reaction

Controlled synthesis of ultrasmall RuP2 particles on N,P-codoped carbon as superior pH-wide electrocatalyst for hydrogen evolution

Crystalline-amorphous Ru@RuP core-shell nanoparticles anchored on carbon nanotubes for enhanced hydrogen evolution electrocatalysis

Facile Synthesis of PdCuRu Porous Nanoplates as Highly Efficient Electrocatalysts for Hydrogen Evolution Reaction in Alkaline Medium

N, P-doped carbon supported ruthenium doped Rhenium phosphide with porous nanostructure for hydrogen evolution reaction using sustainable energies

A Sustainable Route to Ruthenium Phosphide (RuP)/Ru Heterostructures with Electron‐Shuttling of Interfacial Ru for Efficient Hydrogen Evolution

Ruthenium nanoparticles loaded on N/P co-doped carbon sphere derived from sphere cross-linked hydrogel for highly improved hydrogen evolution reaction

Epitaxial Growth Triggered Core-Shell Pd@RuP Nanorods for High-Efficiency Electrocatalytic Hydrogen Evolution

Bigger is Surprisingly Better: Agglomerates of Larger RuP Nanoparticles Outperform Benchmark Pt Nanocatalysts for the Hydrogen Evolution Reaction

Micropore-confined Ru nanoclusters catalyst for efficient pH-universal hydrogen evolution reaction

Efficient and Robust Hydrogen Evolution: Phosphorus Nitride Imide Nanotubes As Supports for Anchoring Single Ruthenium Sites.

Ru-modified cobalt phosphide nanoparticles on N-doped carbon nanofibers for efficient hydrogen evolution reaction in alkaline media

Ultrafine RuP2 nanoparticles supported on nitrogen-doped carbon based on coordination effect for efficient hydrogen evolution

Monodispersed ruthenium nanoparticles interfacially bonded with defective nitrogen-and-phosphorus-doped carbon nanosheets enable pH-universal hydrogen evolution reaction

Supramolecular Anchoring Strategy for Facile Production of Ruthenium Nanoparticles Embedded in N-Doped Mesoporous Carbon Nanospheres for Efficient Hydrogen Generation

Ruthenium-manganese phosphide nanohybrid supported on graphene for efficient hydrogen evolution reaction in acid and alkaline conditions

Encapsulation of ruthenium oxide nanoparticles in nitrogen-doped porous carbon polyhedral for pH-universal hydrogen evolution electrocatalysis

Double-Solvent Induced Ultrafine Ruthenium Nanoparticles on Porous Carbon for Highly Efficient Hydrogen Evolution Reaction

Nitrogen-Doped CoP-Co2P-Supported Ru with Interconnected Channels through a Microwave Quasi-Solid Approach for Hydrogen Evolution Reaction over a Wide pH Range

Size effect of ruthenium nanoparticles on water cracking properties with different crystal planes for boosting electrocatalytic hydrogen evolution