Down-conversion Photoluminescence Properties of YVO4: Eu3+@SiO2 Core-shell Structures for Solar Cell Applications

Tan Man-Lin,Shang Xu-Ran,Ma Qing,Wang Xiao-Wei,Fu Dong-Ju,Li Dong-Shuang,Zhang Wei-Li,Chen Jian-Jun,Zhang Hua-Yu

DOI: https://doi.org/10.15541/jim20160040

2016-01-01

Abstract:Europium ions doped yttrium vanadate (YVO4: Eu3+) has excellent emission properties for down-conversion applications. However, the serious surface defects of YVO4: Eu3+ hinder the improvement of luminescent efficiency. In order to improve the particle size distribution and morphology of YVO4: Eu3+ nano-powders, mono-dispersed spherical YVO4: Eu3+@SiO2 core-shell structure materials were prepared by coating a layer of YVO4: Eu3+ onto the surface of SiO2 microspheres. With the shell-core ratio setting as 0.6, the luminescence intensity of YVO4: Eu3+@SiO2 core-shell structure composite could reach up to more than 90% of pure YVO4: Eu3+ nano-powder. Furthermore, the prepared YVO4: Eu3+@SiO2 core-shell structure films were used as down-conversion materials for amorphous silicon thin film solar cells. The cell parameters such as short current density and photoelectric conversion efficiency increased from original 6.694 mA/cm(2) and 9.40% to 8.417 mA/cm(2) and 10.15%, respectively. Thus YVO4: Eu3+@SiO2 core-shell configuration can be fabricated from YVO4: Eu3+ and SiO2 microsphere to avoid agglomeration. The prepared YVO4: Eu3+@SiO2 core-shell structures have regular morphology and uniform particle sizes, which are suitable to be used as down-conversion light emitting layer in amorphous silicon solar cells.