Impact of P-Doped in Spinel LiNi0.5Mn1.5O4 on Degree of Disorder, Grain Morphology, and Electrochemical Performance

Deng, Yu-Feng,Zhao, Shi-Xi,Xu, Ya-Hui,Gao, Kai,Nan, Ce-Wen

DOI: https://doi.org/10.1021/acs.chemmater.5b03517

IF: 10.508

2015-01-01

Chemistry of Materials

Abstract:LiNi0.5-xP2xMn1.5-xO4(x = 0, 0.005, 0.01, and 0.02) submicrograins in regular octahedral shape with merely {111} surface facets and truncated octahedral shape with both {111} and {100} surface planes were obtained by the solid-state reaction method. The effect of doping P on ions arrangement, grain morphology, and the electrochemical performance of lithium nickel manganese oxide was investigated. The characterizations of X-ray diffraction (XRD), Raman, X-ray photoelectron spectroscopy (XPS), and selected area electron diffraction (SAED) confirm more Mn3+ions in the structure to enhance the cationic disorder degree of LiNi0.5Mn1.5O4after P-doping. Comparing the LiNi0.5Mn1.5O4and LiNi0.495P0.01Mn1.495O4samples both with regular octahedral morpology, their electrochemical performance could be remarkably improved by more disordered transition metal ions arrangement leading to higher conductivity of Li-ions and electrons. However, when the amount of P-doping further increased, the rate and cycle ability of the LiNi0.480P0.04Mn1.480O4sample in truncated octahedral shape worsen dramatically even with a higher degree of cationic disorder. This could be on account of the crystal planes starting to dominate the electrochemical performance instead of ions arrangement under high voltage and large rate: the {111} facet is more favorable to the lithium ion transport than the {100} crystal plane for LiNi0.5Mn1.5O4submicrograins during charge and discharge. 2015 American Chemical Society.