X-ray photoelectron spectroscopy and NIR self-quenching emission behavior in Ho 3+ doped YOF and V-YOF

N.A.M. Saeed,H.C. Swart,E. Coetsee

DOI: https://doi.org/10.1016/j.optmat.2024.115303

IF: 3.754

2024-04-07

Optical Materials

Abstract:Stoichiometric (YOF) and non-stoichiometric yttrium oxyfluoride (Y 7 O 6 F 9 ) also known as the vernier phase (V-YOF) were investigated for possible optical applications. Both structures were prepared from a single source through the pyrolysis method. The V-YOF and YOF structures decomposed at 900 °C and 950 °C, respectively. X-ray photoelectron spectroscopy revealed four different yttrium sites in the V-YOF structure. The visible holmium ions emission doped in both consisted of three regions due to the 5 S 2 , 5 F 4 → 5 I 8 , 5 F 5 → 5 I 8 , and 5 S 2 , 5 F 4 → 5 I 7 transitions. The YOF structure's visible lifetime was also longer than in the V-YOF structure . The near-infrared photoluminescence emission originated from 5 S 2 , 5 F 4 → 5 I 6 , 5 I 6 → 5 I 8 in both structures. The 5 S 2 , 5 F 4 → 5 I 6 near-infrared lifetimes for both decreased, indicating an energy transfer process. The 5 I 6 → 5 I 8 lifetime in both fluctuated due to the possibility of self-quenching through photon-trapping processes. The lifetimes were in the microseconds range.

materials science, multidisciplinary,optics