Flexible Organic–Inorganic Composite Solid Electrolyte with Asymmetric Structure for Room Temperature Solid-State Li-Ion Batteries
Jianli Gai,Furui Ma,Zengqi Zhang,Deye Sun,Yongcheng Jin,Yingjun Guo,Whangi Kim
DOI: https://doi.org/10.1021/acssuschemeng.9b01869
2019-07-24
Abstract:Solid state electrolytes have stimulated research interest due to their promising application in lithium batteries with high safety. In this paper, an asymmetrical structure composite solid electrolyte consisting of Li<sub>1.3</sub>Al<sub>0.3</sub>Ti<sub>1.7</sub>(PO<sub>4</sub>)<sub>3</sub> (LATP), poly(vinylidene fluoride–hexafluoropropylene) (P(VDF-HFP)), succinonitrile (SN), and a polyimide (PI) film (named ACSE-PI) was fabricated successfully. This solid electrolyte is flexible and can be stable at a high temperature of 150 °C. Moreover, it exhibits a wide electrochemical window of 5 V and high ionic conductivity of over 10<sup>–4</sup> S cm<sup>–1</sup>. An all-solid-state battery assembled with this electrolyte exhibits excellent performance at ambient temperature. In particular, the specific discharge capacity of LiFePO<sub>4</sub>/ACSE-PI/Li battery is 168.4, 164.4, 154.9, 143.4, 129.5, and 109.4 mAh g<sup>–1</sup> at a rate of 0.1, 0.2, 0.5, 1, 2, and 5 C, respectively. It also delivers a reversible discharge capacity of 156 mAh g<sup>–1</sup> after 200 cycles at 0.2 C. Notably, the battery can also operate at 4 °C, and the discharge capacity is higher than 110 mAh g<sup>–1</sup> after 200 cycles at 0.2 C. Considering the good performances mentioned above, the ACSE-PI electrolyte is appropriate for the practical application of a solid-state Li-ion battery with higher safety.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology