Jiaqi Cao,Yuansheng Shi,Aosong Gao,Guangyuan Du,Muhtar Dilxat,Yongfei Zhang,Mohang Cai,Guoyu Qian,Xueyi Lu,Fangyan Xie,Yang Sun,Xia Lu
Abstract:Abstract Exploiting thin Li metal anode is essential for high-energy-density battery, but is severely plagued by the poor processability of Li, as well as the uncontrollable Li plating/stripping behaviors and Li/electrolyte interface. Herein, a thickness/capacity-adjustable thin alloy-type Li/LiZn@Cu anode is fabricated for high-energy-density Li metal batteries. The as-formed lithophilic LiZn alloy in Li/LiZn@Cu anode can effectively regulate Li plating/stripping and stabilize the Li/electrolyte interface to deliver the hierarchical Li electrochemistry. Upon charging, the Li/LiZn@Cu anode firstly acts as Li source for homogeneous Li extraction. At the end of charging, the de-alloy of LiZn nanostructures further supplements the Li extraction, actually playing the Li compensation role in battery cycling. While upon discharging, the LiZn alloy forms just at the beginning, thereby regulating the following Li homogeneous deposition. The reversibility of such an interesting process is undoubtedly verified from the electrochemistry and in-situ XRD characterization. This work sheds light on the facile fabrication of practical Li metal anodes and useful Li compensation materials for high-energy-density Li metal batteries.
What problem does this paper attempt to address?
The paper primarily focuses on addressing key issues associated with lithium electrodes in high-energy-density lithium metal batteries, including the processing difficulties of lithium metal, uncontrollable lithium plating/stripping behavior, and the instability of the lithium-electrolyte interface. To tackle these challenges, the research team developed a thin alloy-type lithium/zinc composite anode (Li/LiZn@Cu) with adjustable thickness and capacity, aimed at achieving high-performance lithium metal batteries.
Specifically, by forming a lithium-friendly LiZn alloy on a copper substrate, the lithium plating/stripping process can be effectively regulated, and the interface between lithium and the electrolyte can be stabilized, thereby realizing hierarchical lithium electrochemical reactions. During the charging process, Li/LiZn@Cu initially serves as a source of uniform lithium extraction; at the end of charging, the dealloying of the LiZn nanostructure further supplements lithium extraction, essentially acting as a lithium compensation during battery cycling. During the discharging process, as soon as the LiZn alloy begins to form, it regulates the subsequent uniform deposition of lithium. The reversibility of this interesting process is undoubtedly confirmed through electrochemical and in situ X-ray diffraction characterization.
This work reveals a simple preparation method for practical lithium metal anodes and lithium compensation materials in high-energy-density lithium metal batteries. Since their first commercialization in the 1990s, lithium-ion batteries (LIBs) have dominated the energy storage market for over 30 years due to their high safety, which is imparted by their unique lithium-ion extraction/insertion mechanism. However, despite significant optimization, a substantial gap still exists between the energy density of "rocking-chair" LIBs and the demands of emerging industries. Given the selection of new-generation high-energy-density systems, metallic lithium stands out due to its high capacity (10 times higher than graphite anodes), the lowest redox potential (relative to the standard hydrogen electrode at -3.04 V), and low mass density (0.534 g/cm^3). However, lithium-based battery chemistry involves repetitive lithium plating and stripping processes, during which lithium metal anodes (LMAs) inevitably trigger dendritic deposition and uncontrollable volume changes due to the imperfections of the substrate and "frameless" nature, hindering their further progress from the laboratory to commercialization.
To develop practical LMAs or LMA-based composite materials for high-energy-density LIBs, several effective strategies have been proposed to date. For example, encapsulating metallic lithium into three-dimensional (3D) hosts with high specific surface area and sufficient porosity is a viable method to enhance the reversibility and volume stability of lithium plating/stripping. Moreover, rational design of electrolyte components (such as high-concentration lithium salts and novel additives) or the introduction of artificial solid electrolyte interphase (SEI) can improve the stability of the lithium/electrolyte interface, serving as an indirect strategy to limit LMA and lithium dendrite growth. However, nearly all LMA modifications are based on thick lithium foils (>100 μm, corresponding to an areal capacity >20.5 mAh/cm^2) or thick 3D hosts. Although they have achieved better cycling performance, the excess LMA cannot reasonably match the capacity of current commercial cathodes (such as 3mAh/cm^2) at low N/P ratios (<3), leading to a waste of most lithium sources and compromising energy density. Furthermore, thick modified LMAs, as an infinite source of lithium, cannot reflect the actual effectiveness of the improvement strategies, as lithium losses are continuously replenished during cycling. Therefore, how to prepare thin LMAs (e.g., <50 μm) to better match commercial cathodes and appropriate N/P ratios is of special importance. Overall, the paper aims to address the key challenges of lithium metal batteries through the innovative alloy-type lithium/zinc composite anode, to achieve higher energy density and better performance.