Bimetallic Iron–Cobalt Nanoparticles Coated with Amorphous Carbon for Oxygen Evolution

Xue Bai,Qiang Wang,Jingqi Guan

DOI: https://doi.org/10.1021/acsanm.1c03208

IF: 6.14

2021-10-22

ACS Applied Nano Materials

Abstract:Because of the adjustable electronic structure of bimetallic alloys, they have received much attention in electrocatalytic reactions. However, to date, there is a lack of effective methods to synthesize bimetallic nanoalloys with controllable metal proportions in the active species of the catalysts prepared by a high-temperature annealing method, leading to inferior catalytic activity and difficulty in identifying the active sites. Here, we synthesize iron (Fe)–cobalt (Co)-based nanoparticles coated with a few layers of amorphous carbon shell (<1 nm) and with Co7Fe3 alloy as the core by facile pyrolysis of a bimetallic Fe–Co-based tartrate, which exhibits excellent oxygen evolution reaction (OER) activity with a low overpotential of 272 mV at a current density of 10 mA cm–2 and good durability in alkaline media. Compared with single-metal Fe/Co tartrate-derived catalysts, a bimetallic Fe–Co tartrate-derived catalyst with Co7Fe3O x active sites shows higher charge-transfer ability and a lower OER barrier (approximately 285 kJ mol–1). For the first time, this work demonstrates that Fe–Co-based tartrate complexes can be used as precursors to construct high-performance bimetallic Fe–Co-based nanocomposite catalysts with controllable active sites for electrocatalytic OER.

materials science, multidisciplinary,nanoscience & nanotechnology