Abstract:Conductive copper nanoinks can be used as a low-cost replacement for silver and gold nanoinks that are used in inkjet printing of conductive patterns. We describe a high-throughput, simple, and convenient method for the preparation of copper nanoparticles in aqueous solution at room temperature. Copper acetate is used as the precursor, hydrazine as the reducing agent, and short chain carboxylic acids as capping agents. The concentration of the carboxylic acid plays a key role in the preparation of such copper nanoparticles. Stable copper nanoparticles with a diameter of less than 10 nm and a narrow size distribution were prepared when high concentrations of lactic acid, citric acid, or alanine were used. Thermogravimetric analysis results showed that any lactic acid or glycolic acid adsorbed on the surface of the copper nanoparticles can be removed at a relatively low temperature, especially, glycolic acid, which can be removed from the surface at about 125 °C. Highly conductive copper films prepared using lactic acid and glycolic acid as capping agents were obtained by drop coating a copper nanoparticle paste onto a glass slide followed by low temperature sintering. The electrical resistivity of the copper film using glycolic acid as the capping agent was 25.5 ± 8.0 and 34.8 ± 9.0 μΩ·cm after annealing at 150 and 200 °C for 60 min under nitrogen, respectively. When lactic acid was used as the capping agent, the electrical resistivity of the copper films was 21.0 ± 7.0 and 9.1 ± 2.0 μΩ·cm after annealing at 150 and 200 °C for 60 min under nitrogen, respectively, with the latter being about five times greater than the resistivity of bulk copper (1.7 μΩ·cm).

Facile Synthesis of Copper Nanostructures Through Simple Replacement Reaction

Facile Sulfurization under Ambient Condition with Na2S to Fabricate Nanostructured Copper Sulfide

Facile Synthesis of Air-Stable Nano/submicro Dendritic Copper Structures and Their Anti-Oxidation Properties

Facile and controlled synthesis of copper sulfide nanostructures of varying morphology

Phase-Selective Synthesis and Self-Assembly of Monodisperse Copper Sulfide Nanocrystals

A simple method for the synthesis of copper nanoparticles from metastable intermediates

One-step synthesis of low-dimensional copper-based nanomaterials with intrinsic antioxidant properties

Innovative Multiphase Ultrasonic-Assisted Method for High-Purity, Stable, and Cost-Effective Copper Nanowire Synthesis

Facile and High Yield Replacement Reaction-assisted Synthesis of Silver Dendrites by Jet for Conductive Ink.

One-Pot Fast Synthesis of Leaf-Like CuO Nanostructures and CuO/Ag Microspheres with Photocatalytic Application

Facile Electrochemical Synthesis of Single-Crystalline Copper Nanospheres, Pyramids, and Truncated Pyramidal Nanoparticles from Lithia/Cuprous Oxide Composite Thin Films

Colloidosome-Based Synthesis Of A Multifunctional Nanostructure Of Silver And Hollow Iron Oxide Nanoparticles

Controlled Reactions On A Copper Surface: Synthesis And Characterization Of Nanostructured Copper Compound Films

Morphology and Composition Controlled Synthesis of Flower-Like Silver Nanostructures.

Copper nanoparticles: aqueous phase synthesis and conductive films fabrication at low sintering temperature.

One-Step Synthesis and Assembly of Copper Sulfide Nanoparticles to Nanowires, Nanotubes, and Nanovesicles by a Simple Organic Amine-Assisted Hydrothermal Process

[Inappropriate lactation syndrome and serum prolactin in chronic renal failure (author's transl)].

Controllable Synthesis of Metal Particles by a Direct Current Electrochemical Approach

Facile synthesis of copper sulfide wire/carbon nanotube composite with improved sodium storage performance

Controllable Synthesis of CuS Nanostructures from Self-Assembled Precursors with Biomolecule Assistance

Synthesizing Cu-Sn nanowires alloy in highly-ordered Aluminum Oxide templates by using electrodeposition method